In this study microcrystalline cellulose (MCC) was oxidized by 2,2,6,6-tetramethylpiperidine-1-oxyl radical (TEMPO)-mediated oxidation. The treated cellulose slurry was mechanically homogenized to form a transparent dispersion which consisted of individual cellulose nanofibers with uniform widths of 3-4 nm. Bio-nanocomposite films were then prepared from a polyvinyl alcohol (PVA)-chitosan (CS) polymeric blend with different TEMPO-oxidized cellulose nanofiber (TOCN) contents (0, 0.5, 1.0 and 1.5 wt %) via the solution casting method. The characterizations of pure PVA/CS and PVA/CS/TOCN films were performed in terms of field emission scanning electron microscopy (FESEM), tensile tests, thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), and X-ray diffraction (XRD). The results from FESEM analysis justified that low loading levels of TOCNs were dispersed uniformly and homogeneously in the PVA-CS blend matrix. The tensile strength and thermal stability of the films were increased with the increased loading levels of TOCNs to a maximum level. The thermal study indicated a slight improvement of the thermal stability upon the reinforcement of TOCNs. As evidenced by the FTIR and XRD, PVA and CS were considered miscible and compatible owing to hydrogen bonding interaction. These analyses also revealed the good dispersion of TOCNs within the PVA/CS polymer matrix. The improved properties due to the reinforcement of TOCNs can be highly beneficial in numerous applications.
This work reports synthesis, thin film characterizations, and study of an organic semiconductor 2-aminoanthraquinone (AAq) for humidity and temperature sensing applications. The morphological and phase studies of AAq thin films are carried out by scanning electron microscope (SEM), atomic force microscope (AFM), and X-ray diffraction (XRD) analysis. To study the sensing properties of AAq, a surface type Au/AAq/Au sensor is fabricated by thermally depositing a 60 nm layer of AAq at a pressure of ~10-5 mbar on a pre-patterned gold (Au) electrodes with inter-electrode gap of 45 µm. To measure sensing capability of the Au/AAq/Au device, the variations in its capacitance and resistance are studied as a function of humidity and temperature. The Au/AAq/Au device measures and exhibits a linear change in capacitance and resistance when relative humidity (%RH) and temperature are varied. The AAq is a hydrophobic material which makes it one of the best candidates to be used as an active material in humidity sensors; on the other hand, its high melting point (575 K) is another appealing property that enables it for its potential applications in temperature sensors.