Chemical modification of natural rubber (NR) has frequently been attempted to improve the performance in specific application. 30% poly(methyl metacrylate) (PMMA) grafted into NR (MG30) has been explored as a potential candidate for polymer electrolytes. The complexation effect of salt and plasticizer in polymer host electrolytes had been investigated using FTIR. The carbonyl stretch of MG30 locates at 1729 cm-1, with the addition of lithium trimethanesulfonate (LiCF3SO3) salt, new band evolves at lower frequency region at 1643-1645 cm-1. The nondegenerate vibrational mode of nus(SO3) of salted electrolytes appearing at 1031-1034 cm-1 comes from 'free' trimethanesulfonate anions and the 1040-1046 cm-1 absorption from the monodentate ion paired with triflates. These indicate MG30-salt interaction. When MG30 and ethylene carbonate (EC) formed film, the CH3 asymmetric bend of MG30 appearing at 1447cm-1 is shifted to 1449 cm-1 in the EC-polymer complex. The CO stretching at 1729 cm-1 also shifted to 1728 cm-1. Hence, the EC-MG30 system is complexed to each other. EC-LiCF3SO3 interactions are indicated by the shifting of CO bending band of EC from 718 cm-1 being shifted to 720 cm-1 in the complex. In Li+-EC interaction where the ring breathing region at 897 cm-1 in EC has shifted to 899 cm-1 in EC-salt spectrum. The band appearing at 1643-1645 cm-1 due to the coordination of Li+
The polymer electrolytes composing of the blend of polyvinyl chloride-polymethyl methacrylate (PVC/PMMA) with lithium triflate (LiCF3SO3) as salt, ethylene carbonate (EC) and dibutyl phthalate (DBP) as plasticizers and silica (SiO2) as the composite filler were prepared. FTIR studies confirm the complexation between PVC/PMMA blends. The CCl stretching mode at 834 cm-1 for pure PVC is shifted to 847 cm-1 in PVC-PMMA-LiCF3SO3 system. This suggests that there is interaction between Cl in PVC with Li+ ion from LiCF3SO3. The band due to OCH3 at 1150 cm-1 for PVC-PMMA blend is shifted to 1168 cm-1 in PVC-PMMA-LiCF3SO3 system. This shift is expected to be due to the interaction between Li+ ion and the oxygen atom in PMMA. The symmetric vibration band and the asymmetric vibration band of LiCF3SO3 at 1033 and 1256 cm-1 shifted to 1075 and 1286 cm-1 in the DBP-EC plasticized PVC-PMMA-LiCF3SO3 complexes. The interaction between Li+ ions and SiO2 will lead to an increase in the number of free plasticizers (which does not interact with Li+ ions). When the silica content increases from 2% to 5%, the intensity of the peak at 896 cm-1 (due to the ring breathing vibration of free EC) increases in PVC-PMMA-LiCF3SO3-DBP-EC system.