One of the non-destructive methods used for the identification and verification of metals is by the energy-dispersive X-ray fluorescence (EDXRF) technique. EDXRF analysis provides several important advantages such as simultaneous determination of the elements present, enable to analyse a very wide concentration range, fast analysis with no tedious sample preparation. The paper shows how this technique is developed and applied in the identification and verification of different grades of stainless steels. Comparison of the results obtained from this analysis with certified reference standards show very small differences between them.
A process to produce calcium phosphate biomaterial was done using an organic based diethylhexyl phosphoric acid (DEHPA) as its starting material. The gel obtained from this reaction was used to study calcium phosphate transformation using in-situ XRD with temperature ranges from room temperature to 1300 o C. The results obtained from this analysis show the following phase transformation sequence gel > β-Ca2P2O7 > β-TCP + HA > α-TCP + HA. β-Ca2P2O7 was formed at 400 o C and the sample when heated up to 1000 o C, peaks of β- TCP and HA appeared showing the transformation of the β-Ca2P2O7 phase. When the sample was heated up further to 1200 o C, β-TCP transformed into α-TCP.