The present investigation deals with the development of ethanol-vapour-sensing materials coated with the semiconducting oxide TiO2. Thick films of anatase TiO2 were deposited using the sol-gel dip-coating technique on alumina substrates by conventional alkoxide sol and modified sol added with Degussa P-25 as the sensing medium. It was shown that crystallised TiO2 anatase was obtained at the annealing temperature of 500oC. The fabricated TiO2 sensors exhibited highest sensitivity at the sensing temperature of 350 ºC. Sensitivity towards the ethanol vapour was further increased with UV light effect. The enhancement of the sensitivity of the modified catalytic pellet can be explained by the crystallite of anatase TiO2 and the effect of the photocatalytic of TiO2. The high sensitivity of the TiO2 film deposited with modified sol revealed that the modified sol could be a new alternative in the development of a TiO2 ethanol sensor.
The adsorption of phenol, from aqueous solutions on activated carbon from waste tyres, was studied in a batch system at different initial concentrations (100-500mg/L) at 30°C for 48 hours. The activated carbon was prepared using the two-step physiochemical activation, with potassium hydroxide (KOH) at ratio KOH/char = 5. The carbonization process was done at 800°C for 1 hour with nitrogen flow rate 150ml/min, followed by the activation with the carbon dioxide flow rate 150ml/min at 800°C for 2 hours. The adsorption isotherms were determined by shaking 0.1g of activated carbon with 100ml phenol solutions. The initial and final concentrations of phenol in aqueous solution were analyzed using the UV-Visible Spectrophotometer (Shimadzu, UV-1601) at a wavelength of 270nm. Experimental isotherm data were analyzed using the Langmuir and Freundlich isotherm models.The equilibrium data for phenol adsorption could fit both isotherm models well with the R2 value of 0.9774 and 0.9895, respectively. The maximum adsorption capacity of the adsorbent obtained from the Langmuir model was up to 156.25 mg/g