  1. Mohamed SH, Arifin A, Mohd Ishak ZA, Nizam A, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:147-8.
    PMID: 15468861
    The aim of this study was to evaluate the mechanical properties and glass transition temperature (Tg) of a denture base material prepared from high molecular weight poly methyl methacrylate (PMMA) and alumina (Al2O3). The glass transition temperature was studied by using differential scanning calorimetry (DSC). The effect of powder-to-liquid ratio was investigated. The result showed that the tensile properties and the Tg were slightly effected by the powder-to-liquid ratio. The ratio of 2.2:1 by weight of powder to liquid was found to be the best ratio for mixing the material to give the best result in this formulation.
  2. Nizam A, Mohamed SH, Arifin A, Mohd Ishak ZA, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:145-6.
    PMID: 15468860
    The aim of this study was to evaluate the tensile properties and water absorption of denture base material prepared from high molecular weight poly methyl methacrylate (PMMA) and alumina (Al2O3) as particulate filler. Specimens for mechanical testing were prepared by adding composite powder to the monomer followed by hand mixing as in dental laboratory procedure. The tensile strength of the prepared denture base material was slightly higher than commercial denture base material, while the water absorption was almost the same for all formulation of denture base materials.
  3. Mohamed SH, Arifin A, Mohd Ishak ZA, Nizam A, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:25-6.
    PMID: 15468801
    The aim of this study was to evaluate the effect of powder-to-liquid ratio on the glass transition temperature (Tg) and the tensile properties of denture base material prepared from poly (methyl methacrylate) (PMMA) and hydroxyapatite (HA) previously treated with 3-trimethoxysilylpropyl methacrylate (gamma-MPS). Specimens for mechanical testing were prepared by adding composites powder (PMMA, BPO and HA) to the monomer (MMA and EGDMA) followed by hand mixing as in dental laboratory description usage. The glass transition temperature was studied by using differential scanning calorimetry (DSC). It was observed that the tensile properties and the Tg were affected by the powder-to-liquid ratio. The mechanical characterization of the materials were performed by using single edge notch-tension (SEN-T) specimens; the fracture toughness was slightly higher in formulation which contained HA filler compared to commercial denture base material.