Ni–SiC composite coatings were electrodeposited from a Watts-type bath containing 5 g/l SiC particles in suspension. The particles were dispersed with the aid of mechanical agitation at 75 rpm and 150 rpm. EDX analysis confirmed the existence of Ni and SiC in the coatings. The effects of agitation speed on hardness properties of the coatings were investigated. SEM results showed that lower agitation speed could improve the amount of co-deposited SiC particles and increase the hardness of the composite coatings. The bonding between the Ni metal matrix and the SiC ceramic particles was compact.
A co-deposition of nickel-phosphorus-alumina (NiPA) composite coatings were obtained from an ordinary sulphate-based plating bath consisting of 5 g/l alumina (Al2O3) particles. The particles were dispersed by using mechanical agitation at 125 rpm. The presence of Ni3P and Al2O3 phases in the coatings was confirmed by XRD analysis. SEM/EDX results indicated that a smooth Ni3P coating was obtained and Al2O3 particles were embedded into the coating. Microscopic observation showed that the bonding between the Ni3P metal matrix and the Al2O3 ceramic particles was compact.