The nucleation of carbonate-containing apatite on the biomaterials surface is regarded as a significant stage in bone healing process. In this regard, composites contained hydroxyapatite (Ca10(PO4)6(OH)2, HA), wollastonite (CaSiO3, WS) and polyethersulfone (PES) were synthesized via a simple solvent casting technique. The in-vitro bioactivity of the prepared composite films with different weight ratios of HA and WS was studied by placing the samples in the simulated body fluid (SBF) for 21 days. The results indicated that the the surface of composites containing 2 wt% HA and 4 wt% WS was completely covered by a thick bone-like apatite layer, which was characterized by Grazing incidence X-ray diffraction, attenuated total reflectance-Fourier transform infrared spectrometer, field emission electron microscopy and energy dispersive X-ray analyzer (EDX). The degradation study of the samples showed that the concentration of inorganic particles could not influence the degradability of the polymeric matrix, where all samples expressed similar dexamethasone (DEX) release behavior. Moreover, the in-vitro cytotoxicity results indicated the significant cyto-compatibility of all specimens. Therefore, these findings revealed that the prepared composite films composed of PES, HA, WS and DEX could be regarded as promising bioactive candidates with low degradation rate for bone tissue engineering applications.
The main aim of this study was to evaluate the suitability of sulfonated alginate as a modifying agent to enhance the hemocompatibility of self-fabricated polyethersulfone (PES) hollow fiber membrane for blood detoxification. Sodium alginate was sulfonated with a degree of 0.6 and immobilized on the membrane via surface amination and using glutaraldehyde as cross-linking agent. Coating layer not only improved the membrane surface hydrophilicity, but also induced -39.2 mV negative charges on the surface. Water permeability of the modified membrane was enhanced from 67 to 95 L/m2·h·bar and flux recovery ratio increased more than 2-fold. Furthermore, the modified membrane presented higher platelet adhesion resistance (reduced by more than 90%) and prolonged coagulation time (35 s for APTT and 14 s for PT) in comparison with the pristine PES hollow fiber membrane, which verified the improved anti-thrombogenicity of the modified membrane. On the other hand, obtained membrane after 3 h coating could remove up-to 60% of the uremic toxins. According to the obtained data, sulfonated alginate can be a promising modifying agent for the future blood-contacting membrane and specially blood purification issues.