Single crystals of Cu2ZnGeSe4 and Cu2ZnGeS4 solid solutions were developed and successfully obtained using the chemical vapor transfer method, with iodine acting as a transporter. The structure, compositional dependences of lattice parameters, pycnometric and X-ray densities and microhardness were determined. The chemical composition determined by the X-ray microanalysis satisfactorily corresponds to the nominal one with a tolerance of ±5 %. The XRD analysis showed that all the obtained compounds and their solid solutions have unit cell described by tetragonal symmetry. The attice parameters were found to be а = 5.342 ± 0.005 Å, с = 10.51 ± 0.01 Å for the Сu2ZnGeS4 compound and а = 5.607 ± 0.005 Å, с = 11.04 ± 0.01 Å for the Cu2ZnGeSe4, respectively. Structural studies confirmed the validity of the Vegard's law in relation to the obtained samples. The pycnometric densities of ∼4.28 g/cm3 for the Cu2ZnGeS4 and ∼5.46 g/cm3 for the Cu2ZnGeSe4 were found to be slightly less than their X-ray densities of ∼4.32 g/cm3 and ∼5.52 g/cm3, respectively. The maximum microhardness of ∼398 kg/mm2 for these solid solutions corresponds to x = 0.60. The melt point of the solid solutions increases from ∼1180 °C for the Сu2ZnGeSe4 up to ∼1400 °C for the Сu2ZnGeS4. Based on X-ray fluorescence analysis and DTA data, the phase diagram of the Cu2ZnGeSe4-Cu2ZnGeS4 system was constructed. Analysis of the obtained diagram indicates its first type according to Rozbom's classification.
The polycrystalline SrFe12O19 samples deeply substituted up to at.67% by Al3+, Ga3+, In3+, Co3+, and Cr3+ cations with a high configurational mixing entropy were prepared by solid-phase synthesis. Phase purity and unit cell parameters were obtained from XRD and analyzed versus the average ionic radius of the iron sublattice. The crystallite size varied around ∼4.5 μm. A comprehensive study of the magnetization was realized in various fields and temperatures. The saturation magnetization was calculated using the Law of Approach to Saturation. The accompanying magnetic parameters were determined. The magnetic crystallographic anisotropy coefficient and the anisotropy field were calculated. All investigated magnetization curves turned out to be nonmonotonic. The magnetic ordering and freezing temperatures were extracted from the ZFC and FC curves. The average size of magnetic clusters varied around ∼350 nm. The high values of the configurational mixing entropy and the phenomenon of magnetic dilution were taken into account.