The properties of fibre-reinforced composites are dependent not only on the strength of the reinforcementfibre but also on the distribution of fibre strength and the composition of the chemicals or additivesaddition within the composites. In this study, the tensile properties of abaca fibre reinforced high impactpolystyrene (HIPS) composites, which had been produced with the parameters of fibre loading (30,40,50wt.%), coupling agent maleic anhydride (MAH) (1,2,3 wt%) and impact modifier (4,5,6 wt.%) weremeasured. The optimum amount of MAH is 3% and the impact modifier is 6% and these give the besttensile properties. Meanwhile, Differential Scanning Calorimetry (DSC) was used to study the thermalbehaviour within the optimum conditions of the composites. In this research, glass transitions temperature(Tg) of neat HIPS occurred below the Tg of the optimum condition of composites as the temperature ofan amorphous state. The endothermic peak of the composites was in the range of 430-4350C, includingneat HIPS. It was observed that enthalpy of the abaca fibre reinforced HIPS composites yielded belowthe neat HIPS of 748.79 J/g.
A study on the effects of alkali treatment and compatibilising agent on the tensile properties of pineappleleaf fibre (PALF) reinforced high impact polystyrene (HIPS) composite is presented in this paper. Thetensile properties of natural fibre reinforced polymer composites are mainly influenced by the interfacialadhesion between the matrix and the fibres. In this study, several chemical modifications were employedto improve the interfacial matrix-fibre bonding and this resulted in the enhancement of tensile propertiesof the composites. In this study, the surface modification of pineapple fibre with alkali treatments andcompatibilizer were used to improve the adhesion between hydrophilic pineapple fibre and hydrophobicpolymer matrix. There are two concentrations of NaOH treatments and compatibilizer used in this study,namely, 2 and 4 wt. %. The results show that the alkali treated fibre and the addition of compatibilisingagent in PALF/HIPS composites have improved the tensile strength and tensile modulus of the composites.