The development of anion exchange membranes (AEMs) is hindered by the trade-off of ionic conductivity, alkaline stability, and mechanical properties. Tröger's base polymers (Tb-polymers) are recognized as promising membrane materials to overcome these obstacles. Herein, the AEMs made from Tb-poly(crown ether)s (Tb-PCEs) show good comprehensive performance. The influence of crown ether on the conductivity and alkaline stability of AEMs has been investigated in detail. The formation of hydronium ion-crown ether complexes and an obvious microphase-separated structure formed by the existence of crown ether can enhance the conductivity of the AEMs. The maximum OH- conductivity of 141.5 mS cm-1 is achieved from the Tb-PCEs based AEM (Tb-PCE-1) at 80 °C in ultrapure water. The ion-dipole interaction of the Na+ with crown ether can protect the quaternary ammonium from the attack of OH- to improve the alkaline stability of AEMs. After 675 h of alkaline treatment, the OH- conductivity of Tb-PCE-1 decreases by only 6%. The Tb-PCE-1-based single cell shows a peak power density of 0.202 W cm-2 at 80 °C. The prominent physicochemical properties are attributed to the well-developed microstructure of the Tb-PCEs, as revealed by TEM, AFM, and SAXS observations.
Anion exchange membrane fuel cells (AEMFCs) have emerged as a promising alternative to proton exchange membrane fuel cells (PEMFCs) due to their adaptability to low-cost stack components and non-noble-metals catalysts. However, the poor alkaline resistance and low OH- conductivity of anion exchange membranes (AEMs) have impeded the large-scale implementation of AEMFCs. Herein, the preparation of a new type of AEMs with crown ether macrocycles in their main chains via a one-pot superacid catalyzed reaction was reported. The study aimed to examine the influence of crown ether cavity size on the phase separation structure, ionic conductivity and alkali resistance of anion exchange membranes. Attributed to the self-assembly of crown ethers, the poly (crown ether) (PCE) AEMs with dibenzo-18-crown-6-ether (QAPCE-18-6) exhibit an obvious phase separated structure and a maximum OH- conductivity of 122.5 mS cm-1 at 80 °C (ionic exchange capacity is 1.51 meq g-1). QAPCE-18-6 shows a good alkali resistance with the OH- conductivity retention of 94.5% albeit being treated in a harsh alkali condition. Moreover, the hydrogen/oxygen single cell equipped with QAPCE-18-6 can achieve a peak power density (PPD) of 574 mW cm-2 at a current density of 1.39 A cm-2.