This work focuses on the fabrication of hybrid bio-composites using green epoxy as the matrix material, hemp (H) and sisal (S) fibre mats as the reinforcements. The hybrid composite with sisal/hemp fibres were fabricated by cost effective hand lay-up technique, followed by hot press with different stacking sequences. Static properties of the composites such as tensile, compressive, inter-laminar shear strengths (ILSS) and hardness were examined. The physical properties such as density, void content, water absorption and thickness swelling were also analyzed. The experimental results indicate that hybrid composites exhibited minor variation in tensile strength when the stacking sequence was altered. The hybrid composite with the intercalated arrangement (HSHS) exhibited the highest tensile modulus when compared with the other hybrid counterparts. Hybrid composites (SHHS and HSSH) offered 40% higher values of compressive strength than the other layering arrangements. HHHH sample exhibited the highest ILSS value of 4.08 MPa. Typical failure characteristics of the short beam test such as inter-laminar shear cracks in the transverse direction, micro-buckling and fibre rupture were also observed.
Nanocellulose was extracted from short bast fibers, from hemp (Cannabis sativa L.) plants harvested at seed maturity, non-retted, and mechanically decorticated in a defibering apparatus, giving non-aligned fibers. A chemical pretreatment with NaOH and HCl allowed the removal of most of the non-cellulosic components of the fibers. No bleaching was performed. The chemically pretreated fibers were then refined in a beater and treated with a cellulase enzyme, followed by mechanical defibrillation in an ultrafine friction grinder. The fibers were characterized by microscopy, infrared spectroscopy, thermogravimetric analysis and X-ray diffraction after each step of the process to understand the evolution of their morphology and composition. The obtained nanocellulose suspension was composed of short nanofibrils with widths of 5-12 nm, stacks of nanofibrils with widths of 20-200 nm, and some larger fibers. The crystallinity index was found to increase from 74% for the raw fibers to 80% for the nanocellulose. The nanocellulose retained a yellowish color, indicating the presence of some residual lignin. The properties of the nanopaper prepared with the hemp nanocellulose were similar to those of nanopapers prepared with wood pulp-derived rod-like nanofibrils.