This systematic review evaluated the effects of nano-sized cement particles on the properties of calcium silicate-based cements (CSCs). Using defined keywords, a literature search was conducted to identify studies that investigated properties of nano-calcium silicate-based cements (NCSCs). A total of 17 studies fulfilled the inclusion criteria. Results indicated that NCSC formulations have favourable physical (setting time, pH and solubility), mechanical (push out bond strength, compressive strength and indentation hardness) and biological (bone regeneration and foreign body reaction) properties compared with commonly used CSCs. However, the characterization and verification for the nano-particle size of NCSCs were deficient in some studies. Furthermore, the nanosizing was not limited to the cement particles and a number of additives were present. In conclusion, the evidence available for the properties of CSC particles in the nano-range is deficient-such properties could be a result of additives which may have enhanced the properties of the material.
To incorporate different concentrations of Al2O9Zr3 (1%, 5%, and 10%) nanoparticles (NP) into the ER adhesive and subsequently assess the impact of this addition on the degree of conversion, μTBS, and antimicrobial efficacy. The current research involved a wide-ranging examination that merged various investigative techniques, including the application of scanning electron microscopy (SEM) for surface characterization of NP coupled with energy-dispersive x-ray spectroscopy (EDX), Fourier-transform infrared (FTIR) spectroscopy, μTBS testing, and microbial analysis. Teeth were divided into four groups based on the application of modified and unmodified three-step ER adhesive primer. Group 1 (0% Al2O9Zr3 NPs) Control, Group 2 (1% Al2O9Zr3 NPs), Group 3 (5% Al2O9Zr3 NPs), and Group 4 (10% Al2O9Zr3 NPs). EDX analysis of Al2O9Zr3 NPs was performed showing elemental distribution in synthesized NPs. Zirconium (Zr), Aluminum (Al), and Oxides (O2). After primer application, an assessment of the survival rate of Streptococcus mutans was completed. The FTIR spectra were analyzed to observe the characteristic peaks indicating the conversion of double bonds, both before and after the curing process, for the adhesive Etch and rinse containing 1,5,10 wt% Al2O9Zr3 NPs. μTBS and failure mode assessment were performed using a Universal Testing Machine (UTM) and stereomicroscope respectively. The μTBS and S.mutans survival rates comparison among different groups was performed using one-way ANOVA and Tukey post hoc (p = .05). Group 4 (10 wt% Al2O9Zr3 NPs + ER adhesive) specimens exhibited the minimum survival of S.mutans (0.11 ± 0.02 CFU/mL). Nonetheless, Group 1 (0 wt% Al2O9Zr3 NPs + ER adhesive) displayed the maximum surviving S.mutans (0.52 ± 0.08 CFU/mL). Moreover, Group 2 (1 wt% Al2O9Zr3 NPs + ER adhesive) (21.22 ± 0.73 MPa) samples displayed highest μTBS. However, the bond strength was weakest in Group 1 (0 wt% Al2O9Zr3 NPs + ER adhesive) (14.13 ± 0.32 MPa) study samples. The etch-and-rinse adhesive exhibited enhanced antibacterial activity and micro-tensile bond strength (μTBS) when 1% Al2O9Zr3 NPs was incorporated, as opposed to the control group. Nevertheless, the incorporation of Al2O9Zr3 NPs led to a decrease in DC. RESEARCH HIGHLIGHTS: 10 wt% Al2O9Zr3 NPs + ER adhesive specimens exhibited the minimum survival of S.mutans. 1 wt% Al2O9Zr3 NPs + ER adhesive samples displayed the most strong composite/CAD bond. The highest DC was observed in Group 1: 0 wt% Al2O9Zr3 NPs + ER adhesive.