The aim of this study was to investigate the effect of the surfactant properties of polyvinyl alcohol (PVA) in enhancing the yield of small size microspheres. Naltrexone microspheres were prepared by solvent-solvent extraction evaporation process. PVA of various concentrations were added into the aqueous phase prior to the mixing process. The addition of PVA was expected to influence the shape, size distribution, drug loading and drug release profile. The results indicated that it is desirable to increase the weight fraction of the microspheres with size range below 106 mm for the highest possible yield.
Antibiotic-loaded bone cement has been used as prophylaxis against infection in total joint replacement surgery. Its effect on the mechanical strength of cement is a major concern as high dose of antibiotic was associated with a significant reduction in mechanical strength of bone cement. However, the cut-off antibiotic that weakens the mechanical strength of cement remains to be determined. This study was undertaken to observe the changes in the mechanical properties of bone cement with gradual increments of Cefuroxime antibiotic. Cefuroxime at different doses: 0, 1.5, 3.0 and 4.5gm were added to a packet of 40gm bone cement (Simplex P) and study samples were prepared by using third generation cementing technique. Mechanical impact, flexural and tensile strength were tested on each sample. Significant impact and tensile strength reduction were observed after addition of 4.5 gm of Cefuroxime. However, flexural strength was significantly reduced at a lower dose of 3.0 gm. The maximum dose of Cefuroxime to be safely added to 40mg Surgical Simplex P is 1.5gm when third generation cementing technique is used. Further study is needed to determine whether it is an effective dose as regards to microbiological parameters.