The main prerequisite of an active visible-light-driven photocatalyst is to effectively utilize the visible light to induce electron-hole (e-/h+) pairs of expanded lifetime. To this end, for the first time, the ternary heterojunctions of CeO2/Fe3O4 /Graphene oxide and Ce3+/ Fe3O4 /Graphene oxide (CeO2/Fe3O4/GO and Fe2.8Ce0.2O4/GO) were prepared via facile ultrasonic-assisted procedures and employed for destruction of oxytetracycline (OTC) under visible light irradiation. The changes in the relative crystal structure, morphology, atomic and surface functional group composition, magnetic, and optic properties of magnetite were uncovered by various techniques. The substantial degradation and mineralization of OTC via visible light/Fe2.8Ce0.2O4/GO system were thoroughly discussed in terms of narrowed band gap energy, the principal function of Ce3+/Ce4+ and Fe2+/Fe3+ redox pairs and GO platelets, enhanced charge separation and transfer, and enlarged active surface area. Furthermore, the performance of visible light/Fe2.8Ce0.2O4/GO system was evaluated for treating real wastewater and its efficiency was investigated using a number of enhancers and scavengers. Finally, the generated byproducts in the course of photodegradation were determined and the oxidation pathway, photocatalytic kinetics, and plausible mechanism were proposed. The results confirmed that the introduced Ce ions and graphene oxide sheets boost the photo-catalytic efficiency of magnetite for photodegradation of OTC.
Silver nanoparticles (Ag-NPs) were synthesized into the interlamellar space of montmorillonite (MMT) by using the γ-irradiation technique in the absence of any reducing agent or heat treatment. Silver nitrate and γ-irradiation were used as the silver precursor and physical reducing agent in MMT as a solid support. The MMT was suspended in the aqueous AgNO(3) solution, and after the absorption of silver ions, Ag(+) was reduced using the γ-irradiation technique. The properties of Ag/MMT nanocomposites and the diameters of Ag-NPs were studied as a function of γ-irradiation doses. The interlamellar space limited particle growth (d-spacing [d(s)] = 1.24-1.42 nm); powder X-ray diffraction and transmission electron microscopy (TEM) measurements showed the production of face-centered cubic Ag-NPs with a mean diameter of about 21.57-30.63 nm. Scanning electron microscopy images indicated that there were structure changes between the initial MMT and Ag/MMT nanocomposites under the increased doses of γ-irradiation. Furthermore, energy dispersive X-ray fluorescence spectra for the MMT and Ag/ MMT nanocomposites confirmed the presence of elemental compounds in MMT and Ag-NPs. The results from ultraviolet-visible spectroscopy and TEM demonstrated that increasing the γ-irradiation dose enhanced the concentration of Ag-NPs. In addition, the particle size of the Ag-NPs gradually increased from 1 to 20 kGy. When the γ-irradiation dose increased from 20 to 40 kGy, the particle diameters decreased suddenly as a result of the induced fragmentation of Ag-NPs. Thus, Fourier transform infrared spectroscopy suggested that the interactions between Ag-NPs with the surface of MMT were weak due to the presence of van der Waals interactions. The synthesized Ag/MMT suspension was found to be stable over a long period of time (ie, more than 3 months) without any sign of precipitation.