This study investigates the effects of calcium carbonate (CaCO(3)) nanoparticles on the mechanical and thermal properties and surface morphology of polycaprolactone (PCL)/chitosan nanocomposites. The nanocomposites of PCL/chitosan/CaCO(3) were prepared using a melt blending technique. Transmission electron microscopy (TEM) results indicate the average size of nanoparticles to be approximately 62 nm. Tensile measurement results show an increase in the tensile modulus with CaCO(3) nanoparticle loading. Tensile strength and elongation at break show gradual improvement with the addition of up to 1 wt% of nano-sized CaCO(3). Decreasing performance of these properties is observed for loading of more than 1 wt% of nano-sized CaCO(3). The thermal stability was best enhanced at 1 wt% of CaCO(3) nanoparticle loading. The fractured surface morphology of the PCL/chitosan blend becomes more stretched and homogeneous in PCL/chitosan/CaCO(3) nanocomposite. TEM micrograph displays good dispersion of CaCO(3) at lower nanoparticle loading within the matrix.
We have compared a simple four-strand flexor tendon repair, the single cross-stitch locked repair using a double-stranded suture (dsSCL) against two other four-strand repairs: the Pennington modified Kessler with double-stranded suture (dsPMK); and the cruciate cross-stitch locked repair with single-stranded suture (Modified Sandow). Thirty fresh frozen cadaveric flexor digitorum profundus tendons were transected and repaired with one of the core repair techniques using identical suture material and reinforced with identical peripheral sutures. Bulking at the repair site and tendon-suture junctions was measured. The tendons were subjected to linear load-to-failure testing. Results showed no significant difference in ultimate tensile strength between the Modified Sandow (36.8 N) and dsSCL (32.6 N) whereas the dsPMK was significantly weaker (26.8 N). There were no significant differences in 2 mm gap force, stiffness or bulk between the three repairs. We concluded that the simpler dsSCL repair is comparable to the modified Sandow repair in tensile strength, stiffness and bulking.