Effect of calcined clay and marble dust powder as cementitious material on the mechanical properties and embodied carbon of high strength concrete by using RSM-based modelling

In the last decade, there has been an increase in research on ecologically benign, cost-effective, and socially useful cement alternative materials for concrete. Alternatives involve industrial and agriculture waste, the potential advantages of which may be recognized by recycling, repurposing, and recreating techniques. Important energy reserves and a decrease in Portland cement (PC) consumption may be attained by using these wastes as supplementary and substitute ingredients, contributing to a reduction in carbon dioxide (CO2) production. Consequently, the incorporation of marble dust powder (MDP) and calcined clay (CC) as supplementary cementitious material (SCM) in high strength concrete may lower the environmental effect and reduce the amount of PC in mixes. This study is conducted on concrete containing 0%, 5%, 10%, 15%, and 20% of MDP and CC as cementitious materials alone and in combination. The main objectives of this investigations are to examine the effect of MDP and CC as cementitious materials on the flowability and mechanical characteristics of high strength concrete. In order to examine the ecological effect of CC and MDP, the eco-strength efficiency and embodied carbon were considered. In this context, there are so many trial mixes were performed on cubical specimens for achieving targeted compressive strength about 60 MPa after 28 days. After getting it, a total of 273 concrete specimens (cubes, cylinders, and prisms) were used to test the compressive, splitting tensile, and flexural strength of high strength concrete correspondingly. Moreover, when the amount of MDP and CC as SCM in the mixture grows, the workability of green concrete decreases. In addition, the compressive strength, flexural strength, and splitting tensile strength are increased by 6.38 MPa, 67.66 MPa, and 4.88 MPa, respectively, at 10% SCM (5% MDP and 5% CC) over a period of 28 days. In addition, using ANOVA, response prediction models were generated and confirmed at a 95% level of significance. The R2 values of the models varied from 96 to 99%. Furthermore, increasing the amount of CC and MDP as SCM in concrete also reduces the amount of carbon embedded in the material. It is recommended that the utilization of 10% SCM (5% MDP and 5% CC) in high strength concrete is providing optimum outcomes for construction industry in the field of Civil Engineering.