Hydroxyapatite (HA) has been earmarked as suitable for implantation within the human of its chemical makeup to human bone. In this paper, HA powders were synthesized via the precipitation method where phosphoric acid (H3PO4) was titrated into calcium hydroxide solution [Ca(OH)2]. Two parameters such as temperature and stirring rate were identified as factors that influenced the amount and purity of HA powder. Phase identification of the synthesized powder was done using X-Ray Diffraction (XRD). The results show that HA phase can be synthesized from this titration process of Ca(OH)2 and H3PO4 with yield amount of HA powder around 45 - 61 grams but with less than hundred percent purity. In order to study the effect of heat treatment to HA crystals structure, HA powder was calcined at 850 degrees C for 2 hours. It's found that the degree of crystallinity increases after calcination because of lattice expansion when the materials were heated at higher temperature