The syntheses of salicylideneaniline (L1a) and 4-hydroxybenzalaniline (L1b) was carried out via condensation reaction giving yields of 80.74% and 81.65% respectively. The compounds were characterised by physical and spectroscopic techniques, namely melting point, micro elemental analysis (C, H and N), 1H Nuclear Magnetic Resonance (NMR) and Infrared (IR) spectroscopy. The characteristic n(C=N) peaks were observed at 1615 cm-1 and 1575 cm-1 respectively. Chronoamperometry (CA) was employed to electrodeposit both compounds on mild steel at 0.1 M inhibitor concentration in 0.3 M NaOH at three different potentials, +0.8 V, +1.05 V and +1.7 V. Formation of yellow imine films was observed on the mild steel. The corrosion behaviour of coated and uncoated mild steel was studied using Linear Polarization Resistance (LPR) in 0.5 M NaCl. Coated mild steel showed better corrosion resistance and with the highest inhibition efficiency of 90.34%, L1a provides a better protection against corrosion for mild steel than L1b.