The durability of natural and treated clay soil stabilized with lime and alkaline activation (AA) affected by environmental factors (hot and humid) was determined in this study. Investigation and evaluation on the strength of the soil, moisture content, and volume change of the specimen were determined at each curing period (7, 28, and 90 days) based on the weather conditions. An unconfined compressive strength (UCS) of the specimen at three different wetting/drying cycles (one, three, and five cycles) was determined. The findings show that the strength of the treated specimens fluctuated with increment and decrement strength (one and three cycles) in the range of 1.41 to 1.88 MPa (lime) and 2.64 to 8.29 MPa (AA), while for five cycles with a curing period of 90 days the decrement was in the range of 1.62 to 1.25 MPa and 6.06 to 5.89 MPa for lime and AA, respectively. The decrement percentage for treated samples that were subjected to five cycles of wetting and drying in 90 days was found to be 20.38% (lime) and 38.64% (AA), respectively. Therefore, it can be summarized that wetting/drying cycles have a significant influence on the durability, strength, and the volume changes of the specimens.
In municipal solid waste (MSW) landfills, biodegradation of the organic MSW fraction results in elevated waste and basal liner temperatures which have the potential to cause the clay component of the basal liner to experience severe moisture loss over time and eventually undergo desiccation cracking. Cracking of the basal liner's clay component would result in an uncontrolled release of contaminants into the surrounding environment and ultimately give rise to a variety of major environmental concerns. Accordingly, this study examined the variation of temperature-moisture profiles along the depth of a compacted clay liner (CCL) exposed to different constant elevated waste temperatures (CETs) in the absence and presence of two heat reduction techniques, respectively. Rockwool insulation layers with varying thicknesses and galvanized steel cooling pipes with varying flowrates were introduced separately as the two heat reduction techniques. Introduction of both techniques led to a significant attenuation of the temperature rise and desiccation experienced by the CCL in the face of different CETs. An increase in rockwool thickness increments led to a progressive reduction of CCL temperature, while an increase in flow rate under turbulent condition did not have a significant influence on the temperature and desiccation reduction of the CCL. Nevertheless, the present study certainly highlights the potential of the two proposed heat reduction techniques to minimize desiccation and consequently increase the service life of CCLs exposed to different elevated temperatures in MSW landfills.