The implementation of hard-facing alloy on the existing materials caters the need for high-performance surfaces in terms of wear and high temperatures. The present research explore the effect of Plasma Transferred Arc Welding (PTAW) parameters and powder composition on dilution, microstructure and hardness of the commonly used hard-facing alloy Ni-Cr-Si-B powder. The hard-facing alloy was deposited with three weight proportions of boron (2.5 %, 3 % and 3.5 %). The statistical-based Grey Relational Analysis (GRA) followed by a Machine Learning Algorithm (MLA) was implemented to identify the ideal parameters and degree of significance of each parameter and for the prediction of the responses. The dilution percentage, microstructure analysis, and phase detection were estimated through elemental analysis, Scanning electron Microscopy (SEM) and X-ray Diffraction Analysis (XRD) respectively. The experimental and modelling results revealed that 400 mm/min of scanning speed, 8 gm/min of powder delivery, 14 mm of stand-off distance, and 120 A of current were the optimal parameters along with 3.5 wt% of boron powder composition to yield a better dilution, microstructure and hardness.
Recently, most service or product-oriented industries have been focusing on their activities to uphold the green and sustainable environment protocol owing to the increased environmental pollution. Concerning this issue, industries are now concentrating on developing recyclable or waste materials products. This research advocates developing and validating a banana fiber sandwich composite to promote the beneficial usage of bio-waste. The composite sandwich specimens were fabricated with resin-impregnated woven banana fiber mat as a skin, and the core was reinforced with three different weight percentages (5, 7.5 and 10%) of chopped banana fiber. The sandwich specimens were pressed into a three-point bending test to validate the structural integrity. The flexural characteristics like flexural strength and modulus were examined experimentally, whereas the key strength indices like flexural stiffness and core shear modulus were evaluated analytically. Post-fracture surfaces were studied through a scanning electron microscope to investigate the failure mechanism. The experimental and analytical results indicate that 10% banana fiber content in the sandwich core increases the flexural strength and flexural modulus to 225% and 147%, respectively, compared to the neat epoxy core. The numerical simulation was also performed through FEA to validate the experimental findings. The numerical results are in good concurrence with the experimental one.
Cardiovascular diseases, particularly coronary artery disease, pose big challenges to human life. Deployment of the stent is a preferable treatment for the above-mentioned disease. However, stents are usually made up of shape memory alloy called Nitinol. The poorer surface finish on the machined nitinol stents accelerates the migration of Nickel ions from the implanted nitinol stent, which is considered toxic and can lead to stenosis. The current study deals with controlling surface quality by minimising surface roughness and improving corrosion resistance. Femtosecond laser (fs-laser 10-15 s) micromachining was employed to machine the Nitinol surface to achieve sub-micron surface roughness. The Grey relational analysis (GRA)-coupled design of the experimental technique was implemented to determine optimal levels of four micromachining parameters (laser power, pulse frequency, scanning speed, and scanning pattern) varied at three levels to achieve minimum surface roughness and to maximise the volume ablation. The results show that to yield minimum surface roughness and maximum volume ablation, laser power and scanning speed are in a higher range. In contrast, the pulse frequency is lower, and the scanning pattern is in a zig-zag manner. ANOVA results manifest that scanning speed is the predominant factor in minimising surface roughness, followed by pulse frequency. Furthermore, the corrosion behaviour of the machined nitinol specimens was evaluated, and the results show that specimens with lower surface roughness had lower corrosion rates.
The effect of crump rubber on the dry sliding wear behavior of epoxy composites is investigated in the present study. Wear tests are carried out for three levels of crump rubber (10, 20, and 30 vol.%), normal applied load (30, 40, and 50 N), and sliding distance (1, 3, and 5 km). The wear behavior of crump rubber-epoxy composites is investigated against EN31 steel discs. The hybrid mathematical approach of Taguchi-coupled Grey Relational Analysis (GRA)-Principal Component Analysis (PCA) is used to examine the influence of crump rubber on the tribological response of composites. Mathematical and experimental results reveal that increasing crump rubber content reduces the wear rate of composites. Composites also show a significant decrease in specific wear values at higher applied loads. Furthermore, the coefficient of friction also shows a decreasing trend with an increase in crump rubber content, indicating the effectiveness of reinforcing crump rubber in a widely used epoxy matrix. Analysis of Variance (ANOVA) results also reveal that the crump rubber content in the composite is a significant parameter to influence the wear characteristic. The post-test temperature of discs increases with an increase in the applied load, while decreasing with an increase in filler loading. Worn surfaces are analyzed using scanning electron microscopy to understand structure-property correlations. Finally, existing studies available in the literature are compared with the wear data of the present study in the form of a property map.