The current study aims to explore the impact of palm oil fuel ash (POFA) heat treatment on the strength activity, porosity, and water absorption of cement mortar. The cement mortar mixtures were typically comprising cement or cement in combination with ultrafine treated POFA (u-TPOFA) which is the final form of the treated POFA, sand, water, and a superplasticizer. Before utilizing the u-TPOFA in mortar mixtures, the treatment processes of POFA were undertaken via five steps (drying at 105 ℃, sieving, grinding, heat treatment, re-grinding) to form u-TPOFA. The heat treatment was performed at three different heating temperatures (i.e., 550 ℃, 600 ℃, and 650 ℃). The ratio on mass/mass basis of the blended ordinary Portland cement (OPC) with u-TPOFA was OPC:u-TPOFA of 70%:30%. A total of four mixtures were prepared, consisting of a plain control mixture (designated as PCM) and three mixtures containing 30% of u-TPOFA treated at three different temperatures designated as M1 "550 ℃," M2 "600 ℃," and M3 "650 ℃". The results show that the optimum mixture was M2 which achieved the highest strength activity index (SAI) of 101.84% and 107% among all mixtures at 7 days and 28 days, respectively. Meanwhile, the porosity (P%) and water absorption (Abs%) of M2 exhibited the lowest values of 9.3% and 4.5%, respectively, among all the mixtures at 28 days. This superior performance of u-TPOFA treated at 600 ℃ represented in the M2 mixture was due to the formation of more binding phases consisting of calcium silicate hydrate (C-S-H) type gel originated from a higher pozzolanic reaction and the filler effects caused by the fine u-TPOFA microparticles. These observations were further confirmed by the improved performance of the M2 mix among all the designed mixes which also exhibited better results in terms of bulk density (BD), ultrasonic pulse velocity (UPV), X-ray diffraction (XRD) as well as thermogravimetry (TGA) and field emission scanning electron microscopy (FESEM-EDX) analyses.
This paper evaluates the flowability and strength properties of alkali-activated mortar produced using silicomanganese fume (SiMnF) as the sole binder, combined with alkaline activators and sand, cured at room temperature (23 ± 1 °C). A total of 18 mixes were prepared by varying binder content (370, 470, and 570 kg/m3), alkaline activator content (33, 43, and 53% of binder by weight), and NaOH concentration (8 M and 12 M). The SiMnF-based alkali-activated pastes were characterized using SEM, XRD, and FTIR techniques to study morphology, mineral composition, and functional groups, respectively. Statistical modeling, including analysis of variance (ANOVA) and response surface method (RSM), was performed to optimize the mixes, and a life cycle assessment was conducted to evaluate the environmental impact of the developed SiMnF-based alkali-activated mortars (SiMnF-AAM). The experimental results showed that an optimal mix design with 470 kg/m3 SiMnF, 43% alkaline activator content, and NaOH concentrations of 8 M and 12 M achieved the best balance of flow and strength. XRD and FTIR analyses confirmed that Nchwaningite was the primary reaction product, with secondary phases including magnetite, manganese ferrite, and potassium feldspar, influenced by alkali concentration. The SiMnF-based mixtures had a significantly lower CO₂ footprint (0.08 kg CO₂/kg) compared to the cement-based mix, with alkali activators being the primary contributors to emissions. The developed SiMnF-AAM mixes, cured at room temperature, exhibited improved workability, mechanical properties, and reduced environmental impact, making them adaptive to real-life applications.
Tungsten disulphide (WS2) is a two-dimensional transition-metal dichalcogenide material that can be used to improve the sensitivity of a variety of sensing applications. This study investigated the effect of WS2 coating on tapered region microfiber (MF) for relative humidity (RH) sensing applications. The flame brushing technique was used to taper the standard single-mode fiber (SMF) into three different waist diameter sizes of MF 2, 5, and 10 µm, respectively. The MFs were then coated with WS2 via a facile deposition method called the drop-casting technique. Since the MF had a strong evanescent field that allowed fast near-field interaction between the guided light and the environment, depositing WS2 onto the tapered region produced high humidity sensor sensitivity. The experiments were repeated three times to measure the average transmitted power, presenting repeatability and sensing stability. Each MF sample size was tested with varying humidity levels. Furthermore, the coated and non-coated MF performances were compared in the RH range of 45-90% RH at room temperature. It was found that the WS2 coating on 2 µm MF had a high sensitivity of 0.0861 dB/% RH with linearity over 99%. Thus, MF coated with WS2 encourages enhancement in the evanescent field effect in optical fiber humidity sensor applications.