In this paper, sugar palm nanocellulose fibre-reinforced thermoplastic starch (TPS)/poly (lactic acid) (PLA) blend bionanocomposites were prepared using melt blending and compression moulding with different TPS concentrations (20%, 30%, 40%, 60%, and 80%) and constant sugar palm nanocellulose fibres (0.5%). The physical, mechanical, thermal, and water barrier properties were investigated. The SEM images indicated different TPS loading effects with the morphology of the blend bionanocomposites due to their immiscibility. A high content of TPS led to agglomeration, while a lower content resulted in the presence of cracks and voids. The 20% TPS loading reduced the tensile strength from 49.08 to 19.45 MPa and flexural strength from 79.60 to 35.38 MPa. The thermal stability of the blend bionanocomposites was reduced as the TPS loading increased. The thickness swelling, which corresponded to the water absorption, demonstrated an increasing trend with the increased addition of TPS loading.
Here we report the draft genomes and annotation of four N-acyl homoserine lactone (AHL)-producing members from the family Sphingomonadaceae. Comparative genomic analyses of 62 Sphingomonadaceae genomes were performed to gain insights into the distribution of the canonical luxI/R-type quorum sensing (QS) network within this family. Forty genomes contained at least one luxR homolog while the genome of Sphingobium yanoikuyae B1 contained seven Open Reading Frames (ORFs) that have significant homology to that of luxR. Thirty-three genomes contained at least one luxI homolog while the genomes of Sphingobium sp. SYK6, Sphingobium japonicum, and Sphingobium lactosutens contained four luxI. Using phylogenetic analysis, the sphingomonad LuxR homologs formed five distinct clades with two minor clades located near the plant associated bacteria (PAB) LuxR solo clade. This work for the first time shows that 13 Sphingobium and one Sphingomonas genome(s) contain three convergently oriented genes composed of two tandem luxR genes proximal to one luxI (luxR-luxR-luxI). Interestingly, luxI solos were identified in two Sphingobium species and may represent species that contribute to AHL-based QS system by contributing AHL molecules but are unable to perceive AHLs as signals. This work provides the most comprehensive description of the luxI/R circuitry and genome-based taxonomical description of the available sphingomonad genomes to date indicating that the presence of luxR solos and luxI solos are not an uncommon feature in members of the Sphingomonadaceae family.
Recently, many scientists and polymer engineers have been working on eco-friendly materials for starch-based food packaging purposes, which are based on biopolymers, due to the health and environmental issues caused by the non-biodegradable food packaging. However, to maintain food freshness and quality, it is necessary to choose the correct materials and packaging technologies. On the other hand, the starch-based film's biggest flaws are high permeability to water vapor transfer and the ease of spoilage by bacteria and fungi. One of the several possibilities that are being extensively studied is the incorporation of essential oils (EOs) into the packaging material. The EOs used in food packaging films actively prevent inhibition of bacteria and fungi and have a positive effect on food storage. This work intended to present their mechanical and barrier properties, as well as the antimicrobial activity of anti-microbacterial agent reinforced starch composites for extending product shelf life. A better inhibition of zone of antimicrobial activity was observed with higher content of essential oil. Besides that, the mechanical properties of starch-based polymer was slightly decreased for tensile strength as the increasing of essential oil while elongation at break was increased. The increasing of essential oil would cause the reduction of the cohesion forces of polymer chain, creating heterogeneous matrix and subsequently lowering the tensile strength and increasing the elongation (E%) of the films. The present review demonstrated that the use of essential oil represents an interesting alternative for the production of active packaging and for the development of eco-friendly technologies.
Treated palm oil mill effluents (POME) is of great concern as it still has colour from its dissolved organics which may pollute receiving water bodies. In this study, the removal of colour from treated palm oil mill effluent were investigated through adsorption studies using carbon derived from wastewater sludge (WSC). Sludge from activated sludge plants were dried and processed to produce WSC. In this study, three different bed depths of WSC were used: 5 cm, 10 cm, and 15 cm. For each bed depth, the flowrate was varied at three different values: 100 mL/hr, 50 mL/hr and 25 mL/hr. It was found that at bed depth of 5 cm, the breakthrough curves were occurred at 360 min, 150 min and 15 min for flowrates of 25, 50 and 100 mL/hr respectively. It was observed that at a particular depth the exhaustion time for column reduced as flow rate increases. Kinetic models, Adams-Bohart and Yoon-Nelson were used to analyze the performance of the adsorption. It was found that rate constant for Adams Bohart model decreased with the increase in bed depth. Adsorption capacity obtained from Adams-Bohart model ranged from 2676.19 mg/L up to 8938.78 mg/L. The maximum adsorption capacity increases with smaller bed depth. For Yoon-Nelson model, the rate constant decreases with increase in bed depth. The required time for 50% breakthrough obtained from the models ranged from 17.01 to 104.17 minutes for all three bed depths. The reduction of colour was found to be effective at all bed depths. The experimental data was best described by both models as with higher values of correlation coefficient (R2).
Synthetic plastics are severely detrimental to the environment because non-biodegradable plastics do not degrade for hundreds of years. Nowadays, these plastics are very commonly used for food packaging. To overcome this problem, food packaging materials should be substituted with "green" or environmentally friendly materials, normally in the form of natural fiber reinforced biopolymer composites. Thermoplastic starch (TPS), polylactic acid (PLA) and polybutylene succinate (PBS) were chosen for the substitution, because of their availability, biodegradability, and good food contact properties. Plasticizer (glycerol) was used to modify the starch, such as TPS under a heating condition, which improved its processability. TPS films are sensitive to moisture and their mechanical properties are generally not suitable for food packaging if used alone, while PLA and PBS have a low oxygen barrier but good mechanical properties and processability. In general, TPS, PLA, and PBS need to be modified for food packaging requirements. Natural fibers are often incorporated as reinforcements into TPS, PLA, and PBS to overcome their weaknesses. Natural fibers are normally used in the form of fibers, fillers, celluloses, and nanocelluloses, but the focus of this paper is on nanocellulose. Nanocellulose reinforced polymer composites demonstrate an improvement in mechanical, barrier, and thermal properties. The addition of compatibilizer as a coupling agent promotes a fine dispersion of nanocelluloses in polymer. Additionally, nanocellulose and TPS are also mixed with PLA and PBS because they are costly, despite having commendable properties. Starch and natural fibers are utilized as fillers because they are abundant, cheap and biodegradable.
Throughout the history of power systems, power cables have been used to securely and efficiently distribute electrical energy to the destined locations. Cross-linked polyethylene (XLPE), a commonly used insulator in high-voltage cables, have several desirable properties, such as low dielectric loss, high dielectric constant, high thermal conductivity, enhanced thermal stability, and superior resistance against electrical stress. However, further improvements of XLPE's performance are needed. The incorporation of large specific surface area nanoparticles, such as boron nitride nanosheets and graphene oxide, exhibited a great potential in enhancing XLPE's properties. These nanoparticles create numerous trapping sites, even at small loading levels, due to their large interfacial regions. In addition, voltage stabilisers with polar groups can scavenge high-energy electrons generated by local electric fields, thereby inhibiting the electrical tree growth. Another important aspect of enhancing XLPE's dielectric performance is the inclusion of antioxidants with phenolic groups. These antioxidants react with peroxyl radicals, mitigating their harmful effects. This review summarises the effects of nanoparticles, voltage stabilisers, antioxidants, and polymer amalgamation on dielectric performance of XLPE as an insulation material. The major challenges in dielectric insulation such as breakdown voltage strength, electrical tree growth, structural defect, space charge accumulation, and thermal aging are addressed.