The incorporation of intermittent renewable energy sources into a consistently controlled power transmission system hinges on advancements in energy storage technologies. Sodium ion batteries (SIBs) are emerging as a primary and viable alternative material due to their electrochemical activity, presenting a potential replacement for the next generation of lithium-ion battery (LIB) energy storage materials. However, this transition may necessitate significant alterations in the anode material, given the incompatibility of the current anode with sodium ions and the electrolyte. This review provides a comprehensive summary of various anode materials employed in SIBs, categorized according to their storage mechanisms. Additionally, it explores the growing focus on utilizing hard carbon as an anode material, driven by factors such as its relatively high specific capacity compared to graphite, cost-effective production, and eco-friendly properties as it can be derived from biomass. The review further addresses recent progress in hard carbon, detailing production methods, modifications, challenges, limitations in integrating hard carbon into the anode of SIBs, and suggests potential directions for future research.
Microwave absorption properties were systematically studied for double-layer carbon black/epoxy resin (CB) and Ni0.6Zn0.4Fe2O4/epoxy resin (F) nanocomposites in the frequency range of 8 to 18 GHz. The Ni0.6Zn0.4Fe2O4 nanoparticles were synthesized via high energy ball milling with subsequent sintering while carbon black was commercially purchased. The materials were later incorporated into epoxy resin to fabricate double-layer composite structures with total thicknesses of 2 and 3 mm. The CB1/F1, in which carbon black as matching and ferrite as absorbing layer with each thickness of 1 mm, showed the highest microwave absorption of more than 99.9%, with minimum reflection loss of -33.8 dB but with an absorption bandwidth of only 2.7 GHz. Double layer absorbers with F1/CB1(ferrite as matching and carbon black as absorbing layer with each thickness of 1 mm) structure showed the best microwave absorption performance in which more than 99% microwave energy were absorbed, with promising minimum reflection loss of -24.0 dB, along with a wider bandwidth of 4.8 GHz and yet with a reduced thickness of only 2 mm.