This present study evaluates the effect of silica modulus (Ms) and curing temperature on strengths and the microstructures of binary blended alkali-activated volcanic ash and limestone powder mortar. Mortar samples were prepared using mass ratio of combined Na2SiO3(aq)/10 M NaOH(aq) of 0.5 to 1.5 at an interval of 0.25, corresponding to Ms of 0.52, 0.72, 0.89, 1.05 and 1.18, respectively, and sole 10 M NaOH(aq). Samples were then subjected to ambient room temperature, and the oven-cured temperature was maintained from 45 to 90 °C at an interval of 15 °C for 24 h. The maximum achievable 28-day strength was 27 MPa at Ms value of 0.89 cured at 75 °C. Samples synthesised with the sole 10 M NaOH(aq) activator resulted in a binder with a low 28-day compressive strength (15 MPa) compared to combined usage of Na2SiO3(aq)/10 M NaOH(aq) activators. Results further revealed that curing at low temperatures (25 °C to 45 °C) does not favour strength development, whereas higher curing temperature positively enhanced strength development. More than 70% of the 28-day compressive strength could be achieved within 12 h of curing with the usage of combined Na2SiO3(aq)/10 M NaOH(aq). XRD, FTIR and SEM + EDX characterisations revealed that activation with combined Na2SiO3(aq)/10 M NaOH(aq) leads to the formation of anorthite (CaAl2Si2O8), gehlenite (CaO.Al2O3.SiO2) and albite (NaAlSi3O8) that improve the amorphosity, homogeneity and microstructural density of the binder compared to that of samples synthesised with sole 10 M NaOH(aq).
This paper evaluates the flowability and strength properties of alkali-activated mortar produced using silicomanganese fume (SiMnF) as the sole binder, combined with alkaline activators and sand, cured at room temperature (23 ± 1 °C). A total of 18 mixes were prepared by varying binder content (370, 470, and 570 kg/m3), alkaline activator content (33, 43, and 53% of binder by weight), and NaOH concentration (8 M and 12 M). The SiMnF-based alkali-activated pastes were characterized using SEM, XRD, and FTIR techniques to study morphology, mineral composition, and functional groups, respectively. Statistical modeling, including analysis of variance (ANOVA) and response surface method (RSM), was performed to optimize the mixes, and a life cycle assessment was conducted to evaluate the environmental impact of the developed SiMnF-based alkali-activated mortars (SiMnF-AAM). The experimental results showed that an optimal mix design with 470 kg/m3 SiMnF, 43% alkaline activator content, and NaOH concentrations of 8 M and 12 M achieved the best balance of flow and strength. XRD and FTIR analyses confirmed that Nchwaningite was the primary reaction product, with secondary phases including magnetite, manganese ferrite, and potassium feldspar, influenced by alkali concentration. The SiMnF-based mixtures had a significantly lower CO₂ footprint (0.08 kg CO₂/kg) compared to the cement-based mix, with alkali activators being the primary contributors to emissions. The developed SiMnF-AAM mixes, cured at room temperature, exhibited improved workability, mechanical properties, and reduced environmental impact, making them adaptive to real-life applications.