A novel preparation method of magnetized palm shell waste-based powdered activated carbon (MPPAC, avg. size 112 μm) was developed. The prepared MPPAC was assessed by several physicochemical analyses, and batch tests were performed for ibuprofen (IBP) removal. Field emission scanning electron microscopy (FESEM) and N2 gas isotherms revealed that magnetite and maghemite were homogeneous and deposited mostly on the surface of PPAC without a significant clogging effect on the micropores. Isotherm results showed that 3.8% Fe (w/w) impregnated PPAC [MPPAC-Fe(3.8%)] had about 2.2-fold higher maximum sorption capacity (157.3 mg g-1) and a 2.5-fold higher sorption density (0.23 mg m-2) than pristine PPAC. Both Fourier-transform infrared spectroscopy (FTIR) and isotherm data indicated that the high sorption capacity and density of IBP by MPPAC was primarily attributable to donor-acceptor complexes with the C = O group and dispersive π-π interactions with the carbon surface. Based on kinetic and repeated adsorption tests, pore diffusion was the rate-limiting step, and MPPAC-Fe(3.8%) had about 1.9~2.8- and 9.1~15.8-fold higher rate constants than MPPAC-Fe(8.6%) and palm shell-waste granular activated carbon (PGAC, avg. size 621 μm), respectively. MPPAC showed almost eight fold greater re-adsorption capacity than PPAC due to a thermal catalytic effect of magnetite/maghemite.
Mesoporous silica materials (MSMs) were synthesized economically using silica (SiO2) as a precursor via a modified alkaline fusion method. The MSM prepared at 500°C (MSM-500) had the highest surface area, pore size, and volume, and the results of isotherms and the kinetics of ibuprofen (IBP) removal indicated that MSM-500 had the highest sorption capacity and fastest removal speed vs. SBA-15 and zeolite. Compared with commercial granular activated carbon (GAC), MSM-500 had a ~100 times higher sorption rate at neutral pH. IBP uptake by MSM-500 was thermodynamically favorable at room temperature, which was interpreted as indicating relatively weak bonding because the entropy (∆adsS, -0.07 J mol(-1) K(-1)) was much smaller. Five times recycling tests revealed that MSM-500 had 83-87% recovery efficiencies and slower uptake speeds due to slight deformation of the outer pore structure. In the IBP delivery test, MSM-500 drug loading was 41%, higher than the reported value of SBA-15 (31%). The in vitro release of IBP was faster, almost 100%, reaching equilibrium within a few hours, indicating its effective loading and unloading characteristics. A cost analysis study revealed that the MSM was ~10-70 times cheaper than any other mesoporous silica material for the removal or delivery of IBP.
The present study reports the removal of Bisphenol A (BPA) and Ibuprofen (IBP) using adsorbents prepared from batik sludge. The calcite sludge-aluminum hydroxide (CAl) adsorbent was prepared by calcination and followed by aluminum hydroxide impregnation. The batik sludge and prepared adsorbents were characterized by FESEM, TGA, XRD, FTIR and BET techniques. The maximum adsorption capacity, adsorption time, different initial solution pH, ionic strength and regeneration study of the adsorbents were also investigated. Furthermore, the sorption behavior of the pollutants were studied by the Langmuir and Freundlich isotherms. The deposition of Al(OH)3 enhanced the BPA and IBP adsorption capacity on the CAl surface. The maximum removal capacity of BPA and Ibuprofen were 83.53 mg g-1 and 34.96 mg g-1 for the CAl adsorbent. In addition, the kinetic data for BPA and IBP were fitted to the pseudo first order, pseudo second order, Elovich, parabolic diffusion and power function equations to understand the sorption behavior. The adsorption behavior of BPA and IBP was mainly chemisorption. This study shows that CAl is a promising adsorbent for the removal of BPA and IBP.