Copolyesters of 3-hydroxybutyrate (3HB) and 4-hydroxybutyrate (4HB) were produced by Cupriavidus sp. (USMAA2-4) (DSM 19379) from carbon sources of 1,4-butanediol and gamma-butyrolactone. The composition of copolyesters produced varied from 0 to 45 mol% 4HB, depending on the combination of carbon sources supplied. The P(3HB-co-4HB) films containing Mitragyna speciosa crude extract were prepared with the ratio varying from 10 to 40% (w/w). The in vitro crude extract release of the films was studied in 0.1M phosphate buffer (pH 7.4) at 37 degrees C. Although the release rate was slow, it was maintained at a constant rate. This suggests that the crude extract release was due to the polymer degradation because the amount of crude extract released was consistent. The amount of degradation was based on the films' dry weight loss, decrease in molecular weight and surface morphology changes. The degradation rate increased with the 4HB content. This showed that the polymer degradation is dependant on the molecular weight, crystallinity, thermal properties and water permeability. The different drug loading ratio which led to surface morphology changes also gave an effect on polymer degradation.
Polyhydroxyalkanoates (PHAs) are hydrophobic biodegradable thermoplastics that have received considerable attention in biomedical applications due to their biocompatibility, mechanical properties, and biodegradability. In this study, the degradation rate was regulated by optimizing the interaction of parameters that influence the enzymatic degradation of P(3HB) film using response surface methodology (RSM). The RSM model was experimentally validated yielding a maximum 21 % weight loss, which represents onefold increment in percentage weight loss in comparison with the conventional method. By using the optimized condition, the enzymatic degradation by an extracellular PHA depolymerase from Acidovorax sp. DP5 was studied at 37 °C and pH 9.0 on different types of PHA films with various monomer compositions. Surface modification of scaffold was employed using enzymatic technique to create highly porous scaffold with a large surface to volume ratio, which makes them attractive as potential tissue scaffold in biomedical field. Scanning electron microscopy revealed that the surface of salt-leached films was more porous compared with the solvent-cast films, and hence, increased the degradation rate of salt-leached films. Apparently, enzymatic degradation behaviors of PHA films were determined by several factors such as monomer composition, crystallinity, molecular weight, porosity, and roughness of the surface. The hydrophilicity and water uptake of degraded salt-leached film of P(3HB-co-70%4HB) were enhanced by incorporating chitosan or alginate. Salt-leached technique followed by partial enzymatic degradation would enhance the cell attachment and suitable for biomedical as a scaffold.