Hydroxyapatite, (HA; Ca1O(PO4)6(OH)2) has been successfully applied in medical and dental applications for several years due to its excellent biocompatibility. The usage of HA in Malaysia, however, is limited due to the lack of availability. Therefore the aim of this work is to produce HA materials from both pure chemicals and from Malaysian natural limestone precursors, and to compare their bulk properties. However, parts of Malaysian natural limestone deposits actually consist of a combination of Ca(OH)2 and CaCO3. In order to utilise the limestone to produce HA material, the combination of these commercially pure chemicals as HA precursors should still work. In order to test this hypothesis, two HAs were produced by wet synthesis technique utilising (a) combination of Ca(OH)2 + CaCO3 from pure commercial chemicals [WCC] and (b) a local natural limestone [WL] precursors. The HAs produced; WCC and WL, were compacted into discs and sintered at 1250 degrees C. The characterisations and evaluations conducted were XRD, SEM-EDX, FTIR and shrinkage factor. The results indicate that WL gives slightly better bulk properties compared to WCC.
This study investigates the effects of calcium carbonate (CaCO(3)) nanoparticles on the mechanical and thermal properties and surface morphology of polycaprolactone (PCL)/chitosan nanocomposites. The nanocomposites of PCL/chitosan/CaCO(3) were prepared using a melt blending technique. Transmission electron microscopy (TEM) results indicate the average size of nanoparticles to be approximately 62 nm. Tensile measurement results show an increase in the tensile modulus with CaCO(3) nanoparticle loading. Tensile strength and elongation at break show gradual improvement with the addition of up to 1 wt% of nano-sized CaCO(3). Decreasing performance of these properties is observed for loading of more than 1 wt% of nano-sized CaCO(3). The thermal stability was best enhanced at 1 wt% of CaCO(3) nanoparticle loading. The fractured surface morphology of the PCL/chitosan blend becomes more stretched and homogeneous in PCL/chitosan/CaCO(3) nanocomposite. TEM micrograph displays good dispersion of CaCO(3) at lower nanoparticle loading within the matrix.