Anticorrosion potential of mangrove tannins on aluminium alloys AA6061 in NaCl solution has been studied using potentiodynamic polarisation method and scanning electron microscopy (SEM). The study was carried out in different pH of corrosive medium in the absence and presence of various concentrations of tannin. The corrosion inhibition behaviour of the mangrove tannin on AA6061 aluminium alloy corrosion was found to be dependant on the pH of NaCl solution. Our results showed that the inhibition efficiency increased with increasing tannins concentration in chloride solution at pH 6. Treatment of aluminium alloy 6061 with all concentrations of mangrove tannins reduced the current density, thus decreased the corrosion rate. Tannins behaved as mixed inhibitors at pH 6 and reduction in current density predominantly affected in cathodic reaction. Meanwhile, at pH 12, addition of tannins shifted the corrosion potential to more cathodic potentials and a passivating effect was observed in anodic potentials. SEM studies have shown that the addition of tannins in chloride solution at pH 12 reduced the surface degradation and the formation of pits.
A simple analytical method for the determination of propionic acid and propionates in bakery products using a simple sample preparation procedure is described. The method involves the conversion of propionates to the non-ionized molecular form by adding glacial acetic acid, which is at the same time efficiently extracted into dichloromethane. After vortexing for 1 min, the extract was directly injected into a capillary gas chromatographic column with flame ionization detector. The method was applied for the determination of propionates in 112 commercial bakery samples. The levels of propionic acid plus propionates in bread, cake/ rolls, burger/hot dog buns and pita breads ranged from 197-1273, 98-1846, 546-1932 and 479-1680 µg mL -1 , respectively. No propionate was detected in any of the 36 biscuit samples analyzed.