In this study, a magnetic/polyetherimide-acrylonitrile composite nanofiber membrane with effective adsorption of nickel ions in an aqueous solution was created using a simple electrospinning method. Iron oxide nanoparticles (NPs) were stirred and ultrasonically dispersed into a polyetherimide-acrylonitrile solution to create a homogenous NPs suspension, which was placed in an electrospinning machine to produce a uniform and smooth nanofiber composite membrane. Nanoparticle incorporation into this membrane was confirmed using scanning electron microscope, energy dispersive X-ray spectroscopy (EDX), Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and NPs aqueous stability from a leaching test. The high adsorption capability of the membrane on nickel ions was attributed to the combination of magnetic NPs, polyetherimide-acrylonitrile matrix, and the nanostructure of the membrane. A membrane containing magnetic NPs demonstrated the maximum adsorption capabilities (102 mg/g) of nickel ions in an aqueous solution. Various kinetic and isotherm models were applied to understand the adsorption behavior, such as pseudo-second-order kinetic and Langmuir isotherm models. A polyetherimide-acrylonitrile composite nanofiber membrane containing magnetic NPs could be used as an environmentally friendly and nontoxic adsorbent for the removal of nickel ions in an aqueous medium due to its ease of preparation and use and stability in aqueous mediums.
Radio frequency (RF) magnetron sputtering was used to deposit tungsten disulfide (WS2) thin films on top of soda lime glass substrates. The deposition power of RF magnetron sputtering varied at 50, 100, 150, 200, and 250 W to investigate the impact on film characteristics and determine the optimized conditions for suitable application in thin-film solar cells. Morphological, structural, and opto-electronic properties of as-grown films were investigated and analyzed for different deposition powers. All the WS2 films exhibited granular morphology and consisted of a rhombohedral phase with a strong preferential orientation toward the (101) crystal plane. Polycrystalline ultra-thin WS2 films with bandgap of 2.2 eV, carrier concentration of 1.01 × 1019 cm-3, and resistivity of 0.135 Ω-cm were successfully achieved at RF deposition power of 200 W. The optimized WS2 thin film was successfully incorporated as a window layer for the first time in CdTe/WS2 solar cell. Initial investigations revealed that the newly incorporated WS2 window layer in CdTe solar cell demonstrated photovoltaic conversion efficiency of 1.2% with Voc of 379 mV, Jsc of 11.5 mA/cm2, and FF of 27.1%. This study paves the way for WS2 thin film as a potential window layer to be used in thin-film solar cells.