This study investigated the relationship between leisure-time physical activity and physical fitness (cardiovascular fitness, body fat percentage, flexibility, muscle strength, and endurance) of 10th-grade male students in Oman. Data were collected from 330 students. All participants completed a descriptive questionnaire, a 1 mile walk/run test; a skinfold analysis of the chest, abdomen, and thigh; a sit and reach test; a hand grip test; and a 1-minute sit-up test. Students spent an average of 19.20 ± 6.77 hours on sedentary activities, 3.46 ± 2.11 hours on sports activities, and 11.22 ± 9.24 hours working per week. The students had an average body fat percentage of 6.38% ± 4.67%, muscle strength 38.04 ± 7.55 kg, flexibility 38.01 ± 7.41 cm, abdominal muscle endurance 38.85 ± 8.15 times/min, and cardiovascular endurance 8.10 ± 1.65 minutes.
In this study, nitrogen doped titanium dioxide-based dye-sensitised solar cell was successfully fabricated
using screen printing technique to discover the optimisation of process parameters for the solar cell
efficiency using response surface methodology (RSM). Parameter optimisation has been a major concern
in solar cell fabrication. The selected parameters were: nitrogen concentration (15-25 mg of urea), the
film thickness (25-60 µm) and dye loading time (12-24 hours), the optimum condition which yields the
highest efficiency of 3.5% was at 15 mg nitrogen concentration, 25 µm film thickness and 24-hours dye
loading time. Film thickness was found to have a significant influence on efficiency while the loading
time exceeding 18 hours has the least significant effect.