  1. Huang NM, Mohd. Ambar Yarmo, Yeong SK, Lim HN, Anuar Kassim
    Rheological properties of highly concentrated oil-in-water (O/W) emulsions (HCEs), formed by mixing palm-based nonionic surfactant, C12E6 (HLB = 11.7, CMC = 25μM), water and olive oil volume fraction ≥78vol% were investigated. Samples with lower oil volume fraction (<85%) and surfactant concentration (<8%) exhibited polydispersity of broader droplet size distribution (DSD). In contrast, samples with higher oil volume fraction (>85%) and surfactant concentration (>8%) displayed monodispersity of narrower DSD. The average droplet size decreased with increasing oil volume fraction and surfactant concentration. All frequency sweep experiments exhibited higher G’ than G”, representing the predominantly elastic nature of HCEs. The crossover of the ascendant and descendant flow curves of HCEs with higher oil volume fraction (>85%) and surfactant concentration (>8%) implied a structural build-up that could give rise to very high stability. The high stability was confirmed through accelerated stability test at 40oC for three months.
  2. Mohd Hamzah Harun, Elias Saion, Noorhana Yahya, Anuar Kassim, Hussain, Muhammad Yousuf, Iskandar Shahrim Mustafa, et al.
    MyJurnal
    The composite polymer films of polyvinyl alcohol/polypyrrole/chloral hydrate (PVA-PPy-CH) had been prepared. Effects of γ-rays on the electrical conductivity of the composite polymer films had been investigated by using Inductance Capacitance Resistance meter (LCR) meter at a frequency ranging from 20 Hz to 1 MHz. With the incorporation of chloral hydrate in the polymer sample, the conductivity increased indicates that it is capable to be used as dopant for polymerizing conjugated polymer. The electrical conductivity obtained increased as the dose increased, which is in the order of 10-5 Scm-1 indicates that γ-rays is capable to enhance the electrical conductivity of the composite polymer films. The parameter of s is in the range of 0.31 d s d 0.49 and obeyed simple power law dispersion ωs. The Scanning Electron Microscopy (SEM) micrographs reveal the formation of polypyrrole globules in polyvinyl alcohol matrix which increased as the irradiation dose was increased.
  3. Mohd Hamzah Harun, Elias Saion, Noorhana Yahya, Anuar Kassim, Ekramul Mahmud, Muhammad Yousuf Hussain, et al.
    MyJurnal
    The composite polymer films of polyvinyl alcohol/polypyrrole/chloral hydrate (PVA-PPy-CH) had been prepared. Effects of J-rays on the electrical conductivity of the composite polymer films had
    been investigated by using Inductance Capacitance Resistance meter (LCR) meter at a frequency
    ranging from 20 Hz to 1 MHz. With the incorporation of chloral hydrate in the polymer sample, the conductivity increased indicates that it is capable to be used as dopant for polymerizing conjugated polymer. The electrical conductivity obtained increased as the dose increased, which is in the order of 10-5Scm-1 indicates that J-rays is capable to enhance the electrical conductivity of the composite polymer films. The parameter of s is in the range of 0.31 d s d 0.49 and obeyed simple power law dispersion Zs. The Scanning Electron Microscopy (SEM) micrographs reveal the formation of polypyrrole globules in polyvinyl alcohol matrix which increased as the irradiation dose was increased.