The non-linear refractive index of Ag nano-fluids prepared by γ-radiation method was investigated using a single beam z-scan technique. Under CW 532 nm laser excitation with power output of 40 mW, the Ag nano-fluids showed a large thermal-induced non-linear refractive index. In the present work it was determined that the non-linear refractive index for Ag nano-fluids is -4.80×10-8 cm2/W. The value of Δn0 was calculated to be -2.05×10-4. Our measurements also confirmed that the non-linear phenomenon was caused by the self-defocusing process making them good candidates for non linear optical devices.
The composite polymer films of polyvinyl alcohol/polypyrrole/chloral hydrate (PVA-PPy-CH) had been prepared. Effects of γ-rays on the electrical conductivity of the composite polymer films had been investigated by using Inductance Capacitance Resistance meter (LCR) meter at a frequency ranging from 20 Hz to 1 MHz. With the incorporation of chloral hydrate in the polymer sample, the conductivity increased indicates that it is capable to be used as dopant for polymerizing conjugated polymer. The electrical conductivity obtained increased as the dose increased, which is in the order of 10-5 Scm-1 indicates that γ-rays is capable to enhance the electrical conductivity of the composite polymer films. The parameter of s is in the range of 0.31 d s d 0.49 and obeyed simple power law dispersion ωs. The Scanning Electron Microscopy (SEM) micrographs reveal the formation of polypyrrole globules in polyvinyl alcohol matrix which increased as the irradiation dose was increased.
The composite polymer films of polyvinyl alcohol/polypyrrole/chloral hydrate (PVA-PPy-CH) had been prepared. Effects of J-rays on the electrical conductivity of the composite polymer films had
been investigated by using Inductance Capacitance Resistance meter (LCR) meter at a frequency
ranging from 20 Hz to 1 MHz. With the incorporation of chloral hydrate in the polymer sample, the conductivity increased indicates that it is capable to be used as dopant for polymerizing conjugated polymer. The electrical conductivity obtained increased as the dose increased, which is in the order of 10-5Scm-1 indicates that J-rays is capable to enhance the electrical conductivity of the composite polymer films. The parameter of s is in the range of 0.31 d s d 0.49 and obeyed simple power law dispersion Zs. The Scanning Electron Microscopy (SEM) micrographs reveal the formation of polypyrrole globules in polyvinyl alcohol matrix which increased as the irradiation dose was increased.