Hydrothermal carbonization (HTC) provides alternatives technique to produce a nanosize activated carbon from biomass with a high surface area. Herein, this study we prepared empty fruit bunch-based activated carbon (EFBHAC) using HTC technique. The activated carbon was then functionalized with K2CO3 and Cu(NO3)2 to produce bifunctional nano-catalyst for simultaneous esterification-transesterification of waste cooking oil (WCO). The physicochemical properties were performed i.e. N2 sorptions analysis, TPD-CO2/NH3, FESEM, EDX, FTIR and XRD analysis. The results revealed that produced EFBHAC possessed a BET surface area of 4056.17 m2 g-1, with pore volume of 0.827 cm3 g-1 and 5.42 nm of pore diameter resulting from hydrolysis, dehydration decarboxylation, aromatization and re-condensation during HTC process. Impregnation of EFBHAC with K2CO3 and Cu(NO3)2 granted a high amount of basicity and acidity of 9.21 mmol g-1 and 31.41 mmol g-1, respectively, accountable to high biodiesel yield of 97.1%, produced at the optimum condition of 5 wt% of catalyst loading, 12:1 of methanol to oil molar ratio at 70 °C for 2 h. More than 80% of biodiesel was produced after the 5th cycle depicted the good reusability. The transformations from WCO to biodiesel was confirmed via 1H NMR, FTIR and TGA analysis. Fuel properties revealed kinematic viscosity of 3.3 mm2 s-1, cetane number of 51, flash point of 160.5 °C, cloud and pour point of 11 °C and -3 °C, respectively. These results show the excellent potential of waste materials to prepare bifunctional nano-catalysts to produce higher biodiesel yield which has potential to be commercialized.
The by-product of the previous transesterification, glycerol was utilised as an acid catalyst precursor for biodiesel production. The crude glycerol was treated through the sulfonation method with sulfuric acid and chlorosulfonic acid in a reflux batch reactor giving solid glycerol-SO3H and glycerol-ClSO3H, respectively. The synthesised acidic glycerol catalysts were characterised by various analytical techniques such as thermalgravimetric analyser (TGA), infrared spectroscopy, surface properties adsorption-desorption by nitrogen gas, ammonia-temperature programmed desorption (NH3-TPD), X-ray diffraction spectroscopy (XRD), elemental composition analysis by energy dispersive spectrometer (EDX) and surface micrographic morphologies by field emission electron microscope (FESEM). Both glycerol-SO3H and glycerol-ClSO3H samples exhibited mesoporous structures with a low surface area of 8.85 mm2/g and 4.71 mm2/g, respectively, supported by the microscopic image of blockage pores. However, the acidity strength for both catalysts was recorded at 3.43 mmol/g and 3.96 mmol/g, which is sufficient for catalysing PFAD biodiesel at the highest yield. The catalytic esterification was optimised at 96.7% and 98.2% with 3 wt.% of catalyst loading, 18:1 of methanol-PFAD molar ratio, 120 °C, and 4 h of reaction. Catalyst reusability was sustained up to 3 reaction cycles due to catalyst deactivation, and the insight investigation of spent catalysts was also performed.