Research on different prefabricated cementitious composites for constructing composite concrete columns is comparatively more limited than that of concrete filled steel tube columns. The main objective of this study was to observe the axial compressive behavior of concrete-filled prefabricated cementitious composite tube (CFPCCT) specimens. In the CFPCCT composite column, the spiral steel bar is arranged as a hoop reinforcement in the cementitious tube before its prefabrication. Following this, the concrete is poured into the prefabricated cementitious composite tube. The tube is able to provide lateral confinement and can carry the axial load, which is attributed to the strength of CFPCCT composite column. The effect of tube wall thickness on the behavior of CFPCCT is studied in this research. A total of eight short-scale CFPCCT composite columns, with three different tube wall thicknesses (25 mm, 30 mm and 35 mm), are tested under axial compressive load. The cementitious composite tube-confined specimens showed a 24.7% increment in load-carrying capacity compared to unconfined specimens. Increasing the wall-thickness had a positive impact on the strength and ductility properties of the composite column. However, poor failure behavior was observed for thicker tube wall. Therefore, concrete-filled cementitious composite tube columns can be considered as an alternative and effective way to construct prefabricated concrete columns.
Schmidt rebound hammer test was employed in this study as a nondestructive test. This test method has been universally utilized due to its non-destructiveness for quick and easy assessment of material strength properties and quality of concrete of an existing structure. Industrial waste materials (air-dried alum sludge, treated alum sludge, limestone dust and quarry dust) were employed as replacement material for fine aggregates in this study. A normal strength concrete was designed to achieve 35 MPa at 28 days, with industrial waste materials replacing fine aggregate at different percentages (0%, 5%, 10% and 15%), and then cured for 7, 28 and 180 days. The compressive strength values and rebound numbers for all the mixes obtained were correlated, and a regression equation was established between compressive strength and Schmidt rebound number. The correlation result showed an excellent relationship between rebound number and compressive strength of concrete produced in this study at all curing ages, with correlation coefficients of R2 = 0.98, R2 = 0.99 and R2 = 0.98. The predicted equation showed a strong relationship with the experimental compressive strength. Therefore, it can be used for the prediction of compressive strength of concrete with industrial waste as a replacement for fine aggregate.