Thermoplastic natural rubber sample is found isotropic based on SAXS pattern. Morphological parameter was obtained based on ideal lamellar morphology using 1-D correlation function. The fitting was carried out using Porod tail model and Vonk for back-extrapolated model. It is found that the long period value is 15.7nm which is comparable to results obtained from Lorents corrected profile, 20nm. Crystalline thickness and amorphous thickness was found as 13.4 and 2.31nm respectively
The thermal conductivity of boron carbide filled thermoplastic natural rubber blend composite is studied experimentally as a function of filler loading and filler size. A polymer blend of 60/40 NR/HDPE was used as matrix for incorporation of particulate nano- and micro-sized B4C as filler to form the composite. As the filler loading is increased from 2-10%wt, a reduction and increment of thermal conductivity was observed. The results show at lower filler loading, HDPE crystallinity affects the thermal conductivity up to 4 and 6%wt of filler for nano- and micro-composite respectively. Further increase the loading do not much alter the crystallinity as the filler is distributed in continues phase of NR. The increment of filler amount in the amorphous NR causes the thermal conductivity to gradually increase which indicates the formation of interconnecting filler network structures