Thermoplastic natural rubber sample is found isotropic based on SAXS pattern. Morphological parameter was obtained based on ideal lamellar morphology using 1-D correlation function. The fitting was carried out using Porod tail model and Vonk for back-extrapolated model. It is found that the long period value is 15.7nm which is comparable to results obtained from Lorents corrected profile, 20nm. Crystalline thickness and amorphous thickness was found as 13.4 and 2.31nm respectively