The microstructure, tensile fracture and creep fracture of as-cast beta phase contained γ-TiAl with nominal composition of Ti-48Al-4Cr (at.%) was investigated. The effect of beta phase on tensile and creep strength was determined from fracture analysis. Tensile test were performed at room temperature whereas constant load tensile creep test were performed at temperature 800 0 C and initial stress of 150MPa. Initial as-cast microstructure, microstructure and fracture surface after tensile and creep test were examined using scanning electron microscopy technique. Analysis shows brittle fracture after room temperature tensile test whereas ductile fracture after high temperature creep test. The role of beta phase was discussed. It is concluded that beta phase is sensitive to temperature and detrimental at both room and high temperature.