With an ever-increasing global population, the combustion of fossil fuels has risen immensely to meet the demand for electricity, resulting in significant increase in carbon dioxide (CO2) emissions. In recent years, CO2 separation technology, such as membrane technology, has become highly desirable. Fabricated mixed matrix membranes (MMMs) have the most desirable gas separation performances, as these membranes have the ability to overcome the trade-off limitations. In this paper, blended MMMs are reviewed along with two polymers, namely polyether sulfone (PES) and polyethylene glycol (PEG). Both polymers can efficiently separate CO2 because of their chemical properties. In addition, blended N-methyl-2-pyrrolidone (NMP) and dimethylformamide (DMF) solvents were also reviewed to understand the impact of blended MMMs' morphology on separation of CO2. However, the fabricated MMMs had challenges, such as filler agglomeration and void formation. To combat this, functionalised multi-walled carbon nanotube (MWCNTs-F) fillers were utilised to aid gas separation performance and polymer compatibility issues. Additionally, a summary of the different fabrication techniques was identified to further optimise the fabrication methodology. Thus, a blended MMM fabricated using PES, PEG, NMP, DMF and MWCNTs-F is believed to improve CO2/nitrogen separation.
The carbon dioxide (CO2) separation technology has become a focus recently, and a developed example is the membrane technology. It is an alternative form of enhanced gas separation performance above the Robeson upper bound line resulting in the idea of mixed matrix membranes (MMMs). With attention given to membrane technologies, the MMMs were fabricated to have the most desirable gas separation performance. In this work, blend MMMs were synthesised by using two polymers, namely, poly(ether sulfone) (PES) and poly (ethylene glycol) (PEG). These polymers were dissolved in blend N-methyl-2-pyrrolidone (NMP) and dimethylformamide (DMF) solvents with the functionalised multi-walled carbon nanotubes (MWCNTs-F) fillers by using the mixing solution method. The embedding of the pristine MWCNTs and MWCNTs-F within the new synthesised MMM was then studied towards CO2/N2 separation. In addition, the optimisation of the loading of MWCNTs-F for blend MMM for CO2/N2 separation was also studied. The experimental results showed that the functionalised MWCNTs (MWCNTs-F) were a better choice at enhancing gas separation compared to the pristine MWCNTs (MWCNTs-P). Additionally, the effects of MWCNTs-F at loadings 0.01 to 0.05% were studied along with the polymer compositions for PES:PEG of 10:20, 20:20 and 30:10. Both these parameters of study affect the manner of gas separation performance in the blend MMMs. Overall, the best performing membrane showed a selectivity value of 1.01 + 0.05 for a blend MMM (MMM-0.03F) fabricated with 20 wt% of PES, 20 wt% of PEG and 0.03 wt% of MWCNTs-F. The MMM-0.03F was able to withstand a pressure of 2 bar, illustrating its mechanical strength and ability to be used in the post combustion carbon capture application industries where the flue gas pressure is at 1.01 bar.