This study reported the synthesis and assessment of zinc oxide/iron oxide (ZnO/Fe2O3) nanocomposite as photocatalysts for the degradation of a mixture of methylene red and methylene blue dyes. X-ray diffraction analysis confirms that the crystallite of zinc oxide (ZnO) has a hexagonal wurtzite phase and iron oxide (Fe2O3) has a rhombohedral phase. Fourier Transform Infra-Red spectrum confirms the presence of Zn-O vibration stretching at 428, 480 and 543 cm-1 stretching confirming Fe-O bond formation. Scanning Electron Microscope images exhibited a diverse size and shape of the nanocomposites. The ZnO-90%/Fe2O3-10% and ZnO-10%/Fe2O3-90% nanocomposites reveal good photocatalytic activity with reaction rate constants of 1.5 × 10-2 and 0.66 × 10-2; and 1.3 × 10-2 and 0.60 × 10-2 for methylene blue and methyl red dye respectively. The results revealed that the synthesized ZnO/Fe2O3 nanocomposite is the best catalyst for dye degradation and can be used for industrial applications in future.
Hybrid material of surgical mask activated carbon (SMAC) and Fe2O3 (SMAC-Fe2O3) composite was prepared by simple co-precipitation method and used as potential material for the remediation of 2,4-dicholrophenol (2,4-DCP). The XRD patterns exhibited the presence of SMAC and Fe2O3, FTIR spectrum showed the FeO-carbon stretching at the wavenumber from 400 to 550 cm-1. UV-Vis DRS results showed the band gap was 1.97 eV and 2.05 eV for SMAC-Fe2O3 and Fe2O3, respectively. The SEM images revealed that the Fe2O3 doped onto the fiber morphology of SMAC. The outcomes of the BET examination exhibited a surface area of 195 m2/g and a pore volume of 0.2062 cm3/g for the SMAC/Fe2O3 composite. The batch mode study shows the maximum adsorption and photocatalytic degradation efficacies which were 97% and 78%, respectively. The experimental data was studied with both linear and nonlinear adsorption isotherm and kinetics models. The nonlinear Langmuir isotherm and pseudo-second-order kinetics (PSOK) models have well fit compared with other models. The Langmuir maximum adsorption capacity (qmax) was found 161.60 mg/g. Thermodynamic analysis shows that the 2,4-DCP adsorption onto SMAC-Fe2O3 was a spontaneous and exothermic process. The PSOK assumes that the adsorption process was chemisorption. The photocatalytic degradation rate constant of 2,4-DCP was calculated using pseudo-first-order kinetics (PFOK) and the rate constant for SMAC-Fe2O3 and Fe2O3 were 0.859 × 10-2 min-1 and 0.616 × 10-2 min-1, correspondingly. In addition, the obtained composite exhibited good reusability after a few cycles. These results confirmed that SMAC-Fe2O3 composite is an effective adsorbent and photocatalyst for removing 2,4-DCP pollutants.
Green synthesis of nanomaterials has emerged as an ecofriendly sustainable technology for the removal of dyes in the last few decades. Especially, plant leaf extracts have been considered as inexpensive and effective materials for the synthesis of nanoparticles. In this study, zinc oxide nanoparticles (ZnO NPs) were prepared using leaves extract of Brassica oleracea var. botrytis (BO) by co-precipitation and applied for photocatalytic/antibacterial activity. The synthesized BO-ZnO NPs was characterized by different instrumental techniques. The UV-vis Spectrum of the synthesized material showed maximum absorbance at a wavelength of 311 nm, which confirmed the formation of BO-ZnO NPs. The XRD pattern of BO-ZnO NPs represents a hexagonal wurtzite structure and the average size of particles was about 52 nm. FT-IR spectrum analysis confirms the presence of hydroxyl, carbonyl, carboxylic, and phenol groups. SEM images exhibited a flower like morphology and EDX spectrum confirming the presence of the elements Zn and O. Photo-catalytic activity of BO-ZnO NPs was tested against thiazine dye (methylene blue-MB) degradation under direct sunlight irradiation. Around 80% of the MB dye got degraded at pH 8 under 75 min of sunlight irradiation. Further, the study examined that the antimicrobial and larvicidal activity of BO-ZnO NPs obtained through green synthesis. The antimicrobial study results showed that the BO-ZnO NPs formed zones against bacterial pathogens. The results showed the formation of an inhibition zone against B. subtills (16 mm), S.aureus (13 mm), K. pneumonia (13 mm), and E. coli (9 mm) respectively at a concentration of 100 μg/mL of BO-ZnO NPs. The larvicidal activity of the BO-ZnO NPs was tested against the fourth instar of Culex quinquefasciatus mosquito larvae The LC50 and LC90 values estimated through the larvicidal activity of BO-ZnO NPs were 76.03, 190.03 ppm respectively. Hence the above findings propose the synthesized BO-ZnO NPs by the ecofriendly method can be used for various environmental and antipathogenic applications.