Potential use of tannic acid (TA) as an additive for fabrication of polyvinylidene difluoride (PVDF) membrane was investigated. The TA was introduced by blending into the dope solution with varying concentrations of 0, 1, 1.5, and 2 wt%. The prepared membranes were characterized and evaluated for filtration of humic acid (HA) solution. The stability of the membrane under harsh treatment was also evaluated by one-week exposure to acid and alkaline conditions. The results show that TA loadings enhanced the resulting membrane properties. It increased the bulk porosity, water uptake, and hydrophilicity, which translated into improved clean water flux from 15.4 L/m2.h for the pristine PVDF membrane up to 3.3× for the TA-modified membranes with the 2 wt% TA loading. The flux recovery ratio (FRR) of the TA-modified membranes (FRRs = 78-83%) was higher than the pristine one (FRR = 58.54%), with suitable chemical stability too. The improved antifouling property for the TA-modified membranes was attributed to their enhanced hydrophilicity thanks to improved morphology and residual TA in the membrane matric.
The accumulation of plastic waste has urged researchers to develop methods of waste conversion into valuable products, which is fuel. This study aimed to synthesize Ni embedded onto Aceh natural zeolite (Ni/Aceh-zeolite) as a cheap catalyst which could be used in the reforming process to improve the quality of oil produced from polypropylene (PP) pyrolysis. Ni/Aceh-zeolite was synthesized from Ni(NO3)2·6H2O and acid-activated natural zeolite through impregnation and calcination. The catalyst was found to have particle sizes ranging from 100 to 200 nm of 20 wt% Ni content. The reforming process using Ni/Aceh natural zeolite with Ni loading of 15 wt% yielded the highest amounts of liquid product (yield = 65%) and gasoline fractions (C5-C12, 96.71%). However, the highest high heating value of 45.467 MJ/kg was found in the liquid product obtained with 20% Ni/Aceh-zeolite. In conclusion, Ni/Aceh-zeolite could be used in the reforming process of PP pyrolysis-derived oil, which could reach a quality similar to that of commercial gasoline.
Polydopamine has been widely used as an additive to enhance membrane fouling resistance. This study reports the effects of two-step dopamine-to-polydopamine modification on the permeation, antifouling, and potential anti-UV properties of polyethersulfone (PES)-based ultrafiltration membranes. The modification was performed through a two-step mechanism: adding the dopamine additive followed by immersion into Tris-HCl solution to allow polymerization of dopamine into polydopamine (PDA). The results reveal that the step of treatment, the concentration of dopamine in the first step, and the duration of dipping in the Tris solution in the second step affect the properties of the resulting membranes. Higher dopamine loadings improve the pure water flux (PWF) by more than threefold (15 vs. 50 L/m2·h). The extended dipping period in the Tris alkaline buffer leads to an overgrowth of the PDA layer that partly covers the surface pores which lowers the PWF. The presence of dopamine or polydopamine enhances the hydrophilicity due to the enrichment of hydrophilic catechol moieties which leads to better anti-fouling. Moreover, the polydopamine film also improves the membrane resistance to UV irradiation by minimizing photodegradation's occurrence.
The removal of impurities from water or wastewater by the membrane filtration process has become more reliable due to good hydraulic performance and high permeate quality. The filterability of the membrane can be improved by having a material with a specific pore structure and good hydrophilic properties. This work aims at preparing a polyvinylidene fluoride (PVDF) membrane incorporated with phospholipid in the form of a 2-methacryloyloxyethyl phosphorylcholine, polymeric additive in the form of polyvinylpyrrolidone, and its combination with inorganic nanosilica from a renewable source derived from bagasse. The resulting membrane morphologies were analyzed by using scanning electron microscopy. Furthermore, atomic force microscopy was performed to analyze the membrane surface roughness. The chemical compositions of the resulting membranes were identified using Fourier transform infrared. A lab-scale cross-flow filtration system module was used to evaluate the membrane's hydraulic and separation performance by the filtration of humic acid (HA) solution as the model contaminant. Results showed that the additives improved the membrane surface hydrophilicity. All modified membranes also showed up to five times higher water permeability than the pristine PVDF, thanks to the improved structure. Additionally, all membrane samples showed HA rejections of 75-90%.
This paper reports the fabrication of polyethersulfone membranes via in situ hydrogen peroxide-assisted polymerization of dopamine. The dopamine and hydrogen peroxide were introduced into the dope solution where the polymerization occurred, resulting in a single-step additive formation during membrane fabrication. The effectivity of modification was evaluated through characterizations of the resulting membranes in terms of chemical functional groups, surface morphology, porosity, contact angle, mechanical strength and filtration of humic acid solution. The results confirm that the polydopamine was formed during the dope solution mixing through peroxide-assisted polymerization as proven by the appearance of peaks associated OH and NH groups in the resulting membranes. The presence of polydopamine residual in the membrane matric enhances the pore properties in terms of size and porosity (by a factor of 10), and by lowering the hydrophilicity (from 69° to 53°) which leads to enhanced filtration flux of up to 217 L/m2 h. The presence of the residual polydopamine also enhances membrane surface hydrophilicity which improve the antifouling properties as shown from the flux recovery ratio of > 80%.