Si3N4-TiN composites were prepared by conventional powder processing (SPS1) and in-situ reaction sintering (SPS2). Rapid densification of SPS was achieved for sample SPS1 and SPS2 within a few minutes at low temperature. Sample SPS1 sintered at 1550ºC showed rapid transformation of α to β Si3N4 while for sample SPS2 sintered at 1350ºC, a significant
degree of α to β Si3N4 transformation was achieved. Homogeneous distribution of equiaxed TiN grains in matrix Si3N4 resulting in high hardness (21.7 GPa) and bending strength (621 MPa) for sample SPS1 sintered at 1550ºC. Elongated TiN grains as the reinforcement of Si
3N4 matrix composites was found to increase the toughness (8.39 MPa m1/2) of sample
SPS2 sintered at 1350ºC. The composites prepared by SPS2 sintered at 1250-1350ºC had low electrical resistivity and could be machined by electrical discharge machining (EDM).
Rakaman panggilan katak Borneo daripada genus Hylarana telah dijalankan di tujuh lokasi kajian di Sarawak, Malaysia. Sebanyak 12 individu daripada lima spesies katak Borneo telah berjaya dirakam dan dianalisis. Daripada 38 pembolehubah panggilan, hanya 27 daripadanya dapat menerangkan ciri-ciri panggilan daripada katak Hylarana Borneo. Saiz katak jantan mempengaruhi secara signifikan tenaga panggilan antara 90:50% amplitud puncak, tempoh nadi di antara 50%, nisbah tempoh panggilan untuk mencapai setengah modulasi frekuensi dan kadar ulangan not. Saiz katak Hylarana Borneo sedikit mempengaruhi frekuensi asas dan dominan panggilan. Di samping itu, taburan pembolehubah panggilan katak dan dendogram Euclid menyokong identiti taksonomi bagi setiap spesies katak Borneo Hylarana.