A study was carried out to produce polyurethane (PU) as a wood laminating adhesive from liquefied kenaf core (LKC) polyols by reacting it with toluene-2,4-diisocyanate (TDI) and 1,4-butanediol (BDO). The LKC polyurethane (LKCPU) adhesive has a molecular weight (MW) of 2666, viscosity of 5370 mPa s, and solids content of 86.9%. The average shear strength of the rubberwood (RW) bonded with LKCPU adhesive was 2.9 MPa. Most of the sheared specimens experienced a total adhesive failure. The formation of air bubbles through the liberation of carbon dioxide was observed to reduce the adhesive penetration and bonding strength which was obviously seen on the sheared specimens. The percentage of catalyst used can be varied based on the usage and working time needed. Nonetheless, the physical properties of LKCPU produced in this work had shown good potential as edge-bonding adhesive.
The aim of this work was to study radiation and the effects of temperature on conductivity properties of polyvinyl alcohol (PVA)-based potassium hydroxide (KOH) and propylene carbonate (PC), where the ionic conduction preferentially occurs in the amorphous phase by free radicals ions through gamma-irradiation. Alkaline composite polymer electrolyte (ACPE) consisting of PVA, KOH and PC of different concentration ratios were prepared by solvent-casting technique. The ACPE were irradiated with different doses from 5 kGy up to 200 kGy. The conductivity properties of the electrolyte films were measured at different frequencies in the range 20 Hz to 1 MHz using LCR meter. The results showed that the conductivity properties were dependent on the radiation dose, temperature and the concentration of the polymer blends.