METHODS: Membrane films were prepared from water-soluble O-C solution blended with various concentrations of glycerol to modify the physical properties of the films. In vitro and in vivo biocompatibility evaluations were performed using primary human skin fibroblast cultures and subcutaneous implantation in a rat model, respectively.
RESULTS: Addition of glycerol significantly influenced the barrier and mechanical properties of the films. Water absorption capacity was in the range of 80%-160%, whereas water vapor transmission rate varied from 1,180 to 1,618 g/m2 per day. Both properties increased with increasing glycerol concentration. Tensile strength decreased while elongation at break increased with the addition of glycerol. O-C films were found to be noncytotoxic to human fibroblast cultures and histological examination proved that films are biocompatible.
CONCLUSION: These results indicate that the membrane film from O-C has potential application as a wound-dressing material.
METHODS: A total sample of 90 mandibular premolar teeth was divided into 2 groups (2 × 45 canals): the GP group and ER group. Each group was further divided into 3 subgroups (n = 15): cold lateral compaction (CLC), warm lateral compaction (WLC) and single cone (SC). The teeth were subsequently embedded in resin and sectioned horizontally at 1, 3, 6 and 9 mm. All sections were then viewed with a stereomicroscope at ×40 magnification. The area occupied by core filling materials was determined using Cell^D software.
RESULTS: With CLC, the percentage of core filling materials in the ER group was significantly higher than in the GP group at the 1- and 3-mm levels. Similarly, with WLC, the percentage of core filling material in the ER group was significantly higher than in the GP group at the 1-, 3- and 9-mm levels. With SC, the percentage of core filling materials in the ER group was significantly higher than in the GP group at all levels.
CONCLUSIONS: It can be concluded that the resin-coated GP/EndoREZ® sealer is superior to the gutta-percha/AH Plus in the percentage of core filling material.
MATERIALS AND METHODS: Ninety human single rooted maxillary and mandibular teeth were selected for this study. The teeth were randomly divided into two experimental groups and one control group as follows: Group A (Ethanolic extract of Sapindus Mukorossi), Group B (17% EDTA), and Group C (Distilled water). The root canals of all three groups were prepared with stainless steel K-files by means of the standard step-back technique and irrigated with 5.25% sodium hypo chloride. The teeth were decoronated, following the irrigation and divided longitudinally into two-halves and visualized using scanning electron microscope (SEM) for the amount of smear layer present utilizing the three-point score system. The observations were noted both before and after the treatment. Nonparametric tests were applied for the comparison and p-value ⩽ 0.05 was considered as statistically significant.
RESULTS: It was evident from that smear layer was completely removed in coronal portion of 27 out of 30 teeth in-group A. For middle and apical areas of group A, 24 and 19 teeth showed complete smear layer removal. In-group B it was found that there were 24, 21, and 3 teeth at coronal, middle and apical, areas respectively where smear layer were completely absent. Intra group comparison showed a significant difference (p = 0.002) in smear layer removal was found for group A at coronal, middle and apical thirds. Similarly, a significant difference (p = 0.001) was also found for group B; however heavy smear layer was found among the three parts of the canal for group C.
CONCLUSIONS: Ethanolic extract of Sapindus Mukorossi have higher effectiveness in removing the smear layer from the root canal in comparison to 17% EDTA.