  1. Sajahan NA, Wan Ibrahim WM
    ScientificWorldJournal, 2014;2014:275984.
    PMID: 25383364 DOI: 10.1155/2014/275984
    Due to similarity in composition to the mineral component of bones and human hard tissues, hydroxyapatite with chemical formula Ca10(PO4)6(OH)2 has been widely used in medical field. Both chicken and duck eggshells are mainly composed of calcium carbonate. An attempt has been made to fabricate nanohydroxyapatite (nHA) by chicken (CES) and duck eggshells (DES) as calcium carbonate source (CaCO3). CES and DES were reacted with diammonium hydrogen [(NH4)2HPO4] solution and subjected to microwave heating at 15 mins. Under the effect of microwave irradiation, nHA was produced directly in the solution and involved in crystallographic transformation. Sample characterization was done using by X-ray diffraction (XRD), fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM).
    Matched MeSH terms: Calcium Carbonate/chemical synthesis*
  2. Abu Bakar SH, Hussein Z, Hee SL, Fazan F
    Med J Malaysia, 2004 May;59 Suppl B:81-2.
    PMID: 15468829
    Hydroxyapatite, (HA; Ca1O(PO4)6(OH)2) has been successfully applied in medical and dental applications for several years due to its excellent biocompatibility. The usage of HA in Malaysia, however, is limited due to the lack of availability. Therefore the aim of this work is to produce HA materials from both pure chemicals and from Malaysian natural limestone precursors, and to compare their bulk properties. However, parts of Malaysian natural limestone deposits actually consist of a combination of Ca(OH)2 and CaCO3. In order to utilise the limestone to produce HA material, the combination of these commercially pure chemicals as HA precursors should still work. In order to test this hypothesis, two HAs were produced by wet synthesis technique utilising (a) combination of Ca(OH)2 + CaCO3 from pure commercial chemicals [WCC] and (b) a local natural limestone [WL] precursors. The HAs produced; WCC and WL, were compacted into discs and sintered at 1250 degrees C. The characterisations and evaluations conducted were XRD, SEM-EDX, FTIR and shrinkage factor. The results indicate that WL gives slightly better bulk properties compared to WCC.
    Matched MeSH terms: Calcium Carbonate/chemical synthesis*