METHODS: HA having nanorods structure were synthetized using ultrasonication with precipitation method. HA nanorods were characterized by TEM for average-size/shape. Following phosphoric acid demineralization, dentine specimens were treated with HA-nanorods with/without subsequent HIFU exposure for 5 s, 10 s and 20 s then stored in artificial saliva for 1-month. Dentine specimens were characterized using different SEM and Raman spectroscopic techniques. In addition, the biochemical stability and HA-nanorods were examined using ATR-FTIR to observe attachment of nanoparticles. Also, surface nanoindentation properties were evaluated using AFM in tapping-mode.
RESULTS: HA-nanorods displayed well-defined, homogenous plate-like nanostructure. TEM revealed intact collagen-fibrils network structure with high density due to obliteration of interfibrillar spaces with clear evidence of remineralization in combined HA/HIFU treatment. With HA-nanorods treatment collagen-network structure was visible, consisting of fibrils interlaced into a compact pattern with evidence of minerals deposition. AFM investigation revealed clear mineral formation with the increase of HIFU exposure time. Bands associated with inorganic phase dominate well in HIFU exposed specimens with PO stretching within dentine mineral identified at 960 cm-1. Characteristic dentine structure for control and HIFU 20 s specimens is reflected as oscillatory mean Amide-I intensity with measurement giving a precise sinusoidal response of polarization angle β within dentinal tissue. Nanoindentation testing showed a gradual significant increase in elastic-modulus with the increase in HIFU exposure time after 1-month storage. FTIR spectrum of the HIFU exposed dentine displayed bands at 1650 cm-1, 1580 cm-1 and 1510 cm-1 that can be attributed to Amide-I, II and III.
SIGNIFICANCE: The synergetic effect of HIFU exposure on remineralization potential of demineralized dentine-matrix following nano-hydroxyapatite treatment was revealed. This synergetic effect is dependent on HIFU exposure time.
METHODOLOGY: Three sodium-fluoride(NaF) concentration(0.01%w/v,0.1%w/v and 0.5%w/v respectively)and two poly-γ-glutamic acid(PGGA)concentration(1%w/v and 2%w/v respectively)were prepared in 0.1 M acetic acid(pH4.0)and deionized distilled water.For de/re-mineralisation study, tooth samples (18 teeth varnished, leaving a 2 mm2 window on the mid-buccal surfaces) were immersed in respective acidified NaF and PGGA solutions. The Ca2+ release/uptake was monitored with ISE over 72-hr with increasing pH every 24-h from 4.0 to 6.0.These teeth were later subjected to cross-sectional microhardness to determine integrated mineral recovery of enamel on increasing pH of respective acidified solution.In order to determine mechanism of PGGA,two concentrations of PGGA in deionized-water-solutions were used for tooth samples immersion followed by overnight drying then later subjected to Fourier Transform Infra-Red(FT-IR) analysis.The FT-IR analysis was also carried out on PGGA powder.For control,the experiment was repeated using hydroxyapatite(HAp)pellets.The density of PGGA solutions(1%and2%)was also measured to determine their dynamic viscosities.
RESULTS: The ISE and microhardness testing revealed statistically significant (ρ ≤ 0.05) dissolution inhibition and remineralisation potential for tooth sample treated with acidified 2%PGGA. From the FT-IR spectra, it was observed that the profiles of the enamel and HAp surfaces treated with 1%-and 2%-PGGA solutions were similar to those of PGGA powder.It was found that the viscosity of PGGA increases with increasing concentration.
CONCLUSION: The study implies that 2% PGGA is more effective than NaF as forms a coating layer to protect from demineralisation and promote remineralisation of the tooth surface.
METHODS: Sixty-five cylindrical block of Fuji IX Fast were prepared using split moulds. The demineralizing solution was an acetate buffered demineralizing solution at pH 403. The remineralizing solution was a buffered solution containing 1.5 mM Ca, 0.9 mM P and 10 ppm F at pH 7. The blocks of Fuji IX Fast were subjected either to two-day alternating cycles of remineralization and demineralization for up to 24 days (test); 6 two-day cycles of demineralizing or remineralizing solution separately, or deionized distilled water alone (controls) or were left untreated (base line control). Mineral profiles of Ca, P, Sr and F within 100 microm of the material surface were assessed following 8, 16 and 24 days of treatment (test); 4, 8 or 12 days (controls) or for baseline control samples, using electron probe microanalysis (EPMA).
RESULTS: There were significant changes in mineral profile in the test specimens in terms of Sr and Ca concentrations. A molecule for molecule exchange of these elements resulted between GIC and eluant solutions. Fluoride loss from the GIC occurredto the level comparable with uptake levels recorded in eluant solutions from previous studies. The ionic exchanges appeared to be the result of dissolution followed by an equilibrium-driven diffusion. These exchanges were superficial though substantial.
CONCLUSIONS: Simulated exposure of Fuji IX to the oral environment resulted in an exchange of Ca from the bathing solutions into Fuji IX to replace any Sr which was lost to the GIC. Fluorine loss from the GIC followed previously described patterns. The possible clinical significance of this exchange was discussed.