Plant-mediated synthesis of silver-doped ZnO nanoparticles with high sonocatalytic activity: Sonocatalytic behavior, kinetic and thermodynamic study

Together with the rapid growth of technology, the discharge of wastewater from industry into environment had become a hot topic among society nowadays. More attention had been given to the development of water treatment techniques. In this study, sonocatalysis was proposed to degrade the organic pollutants using silver-doped zinc oxide (Ag-ZnO) nanoparticles which were synthesized via green synthesis process using Clitoria ternatea Linn (Asian Pigeonwings flower). The characterization results revealed that the incorporation of Ag into the ZnO lattice decreased the crystallite size and increased the specific surface area of ZnO nanoparticles. It is noteworthy that about 98% of sonocatalytic degradation efficiency of malachite green (MG) was successfully achieved within 30 min in the presence of 5 wt.% Ag-ZnO with 1.0 g/L of catalyst loading under 500 mg/L of initial dye concentration, 80 W of ultrasonic power, 45 kHz of ultrasound frequency, and 2.0 mM of oxidant concentration. The kinetic study showed that the sonocatalytic degradation of organic dye was fitted well into second-order kinetic model with high R2 value (0.9531). In the thermodynamic study, negative value of standard Gibbs free energy and low value of activation energy (+ 24.43 kJ/mol) were obtained in the sonocatalytic degradation of MG using the green-synthesized Ag-ZnO sample. HIGHLIGHTS: • Facile synthesis of silver-doped zinc oxide nanoparticles using plant extract which act as reducing and stabilizing agents • Optical, physical, and chemical characterization of green-synthesized nanomaterials were performed • Evaluation of sonocatalytic degradation of organic dye using green-synthesized nanomaterials • Sonocatalytic behavior, kinetic and thermodynamic studies of sonocatalytic reaction.