The term microfibril angle, MFA in wood science refers to the angle between the direction of the helical windings of cellulose microfibrils in the secondary cell wall, S2 layer of fibres and tracheids and the long axis of the cell. In this study, the mean MFA of the cell walls were determined for thin samples of thickness 200.0 µm from pith and outwards, for eight ages of Acacia mangium wood. The determination of MFA was based on a diffraction pattern arising from cellulose crystal planes of the type 002 generated by x-ray diffraction and recorded using an electronic detector. The results show an inversely relationship between MFA and age of tree in Acacia mangium wood. MFA decreased from 26.13° at age 3 year-old to 0.20° at tree of age 15 year-old for the pith region. The most significant drop occurred from 16.14° at age 7 yearold to 11.30° at age 9 year-old. An inversely relationship between MFA and storage modulus E’ was evidence in Acacia mangium at age 10-year-old. The results showed that about 76.22% variation of loss modulus E” was attributed to the MFA, while about 66.4% of the variation of glass transition Tg was explained by MFA under the same experimental conditions.