Owing to the high potential application need in the aerospace and structural industry for honeycomb sandwich composite, the study on the flexural behaviour of sandwich composite structure has attracted attention in recent decades. The excellent bending behaviour of sandwich composite structures is based on their facesheet (FS) and core materials. This research studied the effect of woven glass-fibre prepreg orientation on the honeycomb sandwich panel. A three-point bending flexural test was done as per ASTM C393 standard by applying a 5 kN load on different orientation angles of woven glass-fibre prepreg honeycomb sandwich panel: α = 0°, 45° and 90°. The results show that most of the sandwich panel has almost the same failure mode during the three-point bending test. Additionally, the α = 0° orientation angle shows a higher maximum load prior to the first failure occurrence compared to others due to higher flexibility but lower stiffness. In addition, the woven glass-fibre prepreg orientation angle, α = 0°, has the maximum stress and flexural modulus, which directly depend upon the maximum load value obtained during the flexural test. In addition, the experimental results and analytical prediction for honeycomb sandwich deflection show good agreement. According to the result obtained, it is revealed that woven glass-fibre honeycomb sandwich panels with an α = 0° orientation is a good alternative compared to 45° and 90°, especially when better bending application is the main purpose. The final result of this research can be applied to enhance the properties of glass-fibre-reinforced polymer composite (GFRPC) cross-arm and enhance the existing cross-arm used in high transmission towers.
This research examines the impact of self-polymerized polydopamine (PDA) coating on the mechanical properties and microstructural behavior of polylactic acid (PLA)/kenaf fiber (KF) composites in fused deposition modeling (FDM). A biodegradable FDM model of natural fiber-reinforced composite (NFRC) filaments, coated with dopamine and reinforced with 5 to 20 wt.% bast kenaf fibers, was developed for 3D printing applications. Tensile, compression, and flexural test specimens were 3D printed, and the influence of kenaf fiber content on their mechanical properties was assessed. A comprehensive characterization of the blended pellets and printed composite materials was performed, encompassing chemical, physical, and microscopic analyses. The results demonstrate that the self-polymerized polydopamine coating acted as a coupling agent, enhancing the interfacial adhesion between kenaf fibers and the PLA matrix and leading to improved mechanical properties. An increase in density and porosity was observed in the FDM specimens of the PLA-PDA-KF composites, proportional to their kenaf fiber content. The enhanced bonding between kenaf fiber particles and the PLA matrix contributed to an increase of up to 13.4% for tensile and 15.3% for flexural in the Young's modulus of PLA-PDA-KF composites and an increase of up to 30% in compressive stress. The incorporation of polydopamine as a coupling agent in the FDM filament composite led to an improvement in tensile, compressive, and flexural stresses and strain at break, surpassing that of pure PLA, while the reinforcement provided by kenaf fibers was enhanced more by delayed crack growth, resulting in a higher strain at break. The self-polymerized polydopamine coatings exhibit remarkable mechanical properties, suggesting their potential as a sustainable material for diverse applications in FDM.
Today, additive manufacturing (AM) is the most recent technology used to produce detailed and complexly built parts for a variety of applications. The most emphasis has been given to fused deposition modeling (FDM) in the development and manufacturing fields. Natural fibers have received attention in the area of 3D printing to be employed as bio-filters with thermoplastics, which have prompted an effort for more ecologically acceptable methods of manufacturing. The development of natural fiber composite filaments for FDM requires meticulous methods and in-depth knowledge of the properties of natural fibers and their matrices. Thus, this paper reviews natural fiber-based 3D printing filaments. It covers the fabrication method and characterization of thermoplastic materials blended with natural fiber-produced wire filament. The characterization of wire filament includes the mechanical properties, dimension stability, morphological study, and surface quality. There is also a discussion of the difficulties in developing a natural fiber composite filament. Last but not least, the prospects of natural fiber-based filaments for FDM 3D printing are also discussed. It is hoped that, after reading this article, readers will have enough knowledge regarding how natural fiber composite filament for FDM is created.
Biocomposites are materials that are easy to manufacture and environmentally friendly. Sugar palm fibre (SPF) is considered to be an emerging reinforcement candidate that could provide improved mechanical stiffness and strength to the biocomposites. Numerous studies have been recently conducted on sugar palm biocomposites to evaluate their physical, mechanical and thermal properties in various conditions. Sugar palm biocomposites are currently limited to the applications of traditional household products despite their good thermal stability as a prospective substitute candidate for synthetic fibres. Thus, thermal analysis methods such as TGA and DTG are functioned to determine the thermal properties of single fibre sugar palm composites (SPCs) in thermoset and thermoplastic matrix as well as hybrid SPCs. The biocomposites showed a remarkable change considering thermal stability by varying the individual fibre compositions and surface treatments and adding fillers and coupling agents. However, literature that summarises the thermal properties of sugar palm biocomposites is unavailable. Particularly, this comprehensive review paper aims to guide all composite engineers, designers, manufacturers and users on the selection of suitable biopolymers for sugar palm biocomposites for thermal applications, such as heat shields and engine components.
Compressive strength is an important property in construction material, particularly for thermal insulation purposes. Although the insulation materials possess high fire-retardant characteristics, their mechanical properties are relatively poor. Moreover, research on the correlation between fire-retardant and compressive strength of rice husk ash (RHA)-based geopolymer binder (GB) is rather limited. In addition, previous studies on RHA-based GB used the less efficient one-factor-at-a-time (OFAT) approach. In understanding the optimum value and significant effect of factors on the compressive strength, it was deemed necessary to employ statistical analysis and a regression coefficient model (mathematical model). The objective of the study is to determine the effect of different material behavior, namely brittle and ductile, on the compressive strength properties and the optimum material formulation that can satisfy both compressive strength and fire-retardant properties. The factors chosen for this study were the rice husk ash/activated alkaline solution (RHA/AA) ratio and the sodium hydroxide (NaOH) concentration. Compressive strength and fire-retardant tests were conducted as part of the experiments, which were designed and analyzed using the response surface methodology (RSM). The microstructure of geopolymer samples was investigated using a scanning electron microscope (SEM). Results showed that RHA/AA ratio was highly significant (p < 0.000) followed by NaOH concentration (p < 0.024). When the RHA/AA ratio was at 0.7 to 0.8 and the NaOH concentration was between 12 and 14 M, high compressive strength above 28 MPa was recorded. Optimum compressive strength of approximately 47 MPa was achieved when the RHA/AA ratio and NaOH concentration were 0.85 and 14 M, respectively. Brittle samples with low Si/Al ratio of 88.95 were high in compressive strength, which is 33.55 MPa, and showed a high degree of geopolymerization. Inversely, ductile samples showed low compressive strength and degree of geopolymerization. Water content within the geopolymer binder had a major effect on its fire-retardant properties. Semi-ductile GB showed the best fire-retardant properties, followed by semi-brittle and brittle GB. Using RHA as an aluminosilicate source has proven to be a promising alternative.
Fused deposition modelling (FDM) is a filament-based rapid prototyping technology that allows new composite materials to be introduced into the FDM process as long as they can be manufactured in feedstock filament form. The purpose of this research was to analyze the rheological behavior of oil palm fiber-reinforced acrylonitrile butadiene styrene (ABS) composites when used as a feedstock material, as well as to determine the best processing conditions for FDM. The composite's shear thinning behavior was observed, and scanning electron microscopy was used to reveal its composition. The morphological result found that there was a good fiber/matrix adhesion with a 3 wt% fiber loading, as no fiber pullouts or gaps developed between the oil palm fiber and ABS. However, some pores and fiber pullouts were found with a 5 and 7 wt% fiber loading. Next, the rheological results showed that the increment of fiber content (wt%) increased the viscosity. This discovery can definitely be used in the extrusion process for making wire filament for FDM. The shear thinning effect was increased by adding 3, 5, or 7 wt% of oil palm fiber. The non-Newtonian index (n) of the composites increased as the number of shear rates increased, indicating that the fiber loading had a significant impact on the rheological behavior. As the fiber loading increased, the viscosity and shear stress values increased as well. As a result, oil fiber reinforced polymer composites can be used as a feedstock filament for FDM.
Geopolymer using aluminosilicate sources, such as fly ash, metakaolin and blast furnace slag, possessed excellent fire-retardant properties. However, research on the fire-retardant properties and thermal properties of geopolymer coating using rice husk ash (RHA) is rather limited. Additionally, the approach adopted in past studies on geopolymer coating was the less efficient one-factor-at-a-time (OFAT). A better approach is to employ statistical analysis and a regression coefficient model (mathematical model) in understanding the optimum value and significant effect of factors on fire-retardant and thermal properties of the geopolymer coating. This study aims to elucidate the significance of rice husk ash/activated alkaline solution (RHA/AA) ratio and NaOH concentration on the fire-retardant and thermal properties of RHA-based geopolymer coating, determine the optimum composition and examine the microstructure and element characteristics of the RHA-based geopolymer coating. The factors chosen for this study were the RHA/AA ratio and the NaOH concentration. Rice husk was burnt at a temperature of approximately 600 °C for 24 h to produce RHA. The response surface methodology (RSM) was used to design the experiments and conduct the analyses. Fire-retardant tests and thermal and element characteristics analysis (TGA, XRD, DSC and CTE) were conducted. The microstructure of the geopolymer samples was investigated by using a scanning electron microscope (SEM). The results showed that the RHA/AA ratio had the strongest effect on the temperature at equilibrium (TAE) and time taken to reach 300 °C (TT300). For the optimization process using RSM, the optimum value for TAE and TT300 could be attained when the RHA/AA ratio and NaOH concentration were 0.30 and 6 M, respectively. SEM micrographs of good fire-resistance properties showed a glassy appearance, and the surface coating changed into a dense geopolymer gel covered with thin needles when fired. It showed high insulating capacity and low thermal expansion; it had minimal mismatch with the substrate, and the coating had no evidence of crack formation and had a low dehydration rate. Using RHA as an aluminosilicate source has proven to be a promising alternative. Using it as coating materials can potentially improve fire safety in the construction of residential and commercial buildings.
A novel nanomaterial, bacterial cellulose (BC), has become noteworthy recently due to its better physicochemical properties and biodegradability, which are desirable for various applications. Since cost is a significant limitation in the production of cellulose, current efforts are focused on the use of industrial waste as a cost-effective substrate for the synthesis of BC or microbial cellulose. The utilization of industrial wastes and byproduct streams as fermentation media could improve the cost-competitiveness of BC production. This paper examines the feasibility of using typical wastes generated by industry sectors as sources of nutrients (carbon and nitrogen) for the commercial-scale production of BC. Numerous preliminary findings in the literature data have revealed the potential to yield a high concentration of BC from various industrial wastes. These findings indicated the need to optimize culture conditions, aiming for improved large-scale production of BC from waste streams.
Natural fibers have attracted great attention from industrial players and researchers for the exploitation of polymer composites because of their "greener" nature and contribution to sustainable practice. Various industries have shifted toward sustainable technology in order to improve the balance between the environment and social and economic concerns. This manuscript aims to provide a brief review of the development of the foremost natural fiber-reinforced polymer composite (NFRPC) product designs and their applications. The first part of the manuscript presents a summary of the background of various natural fibers and their composites in the context of engineering applications. The behaviors of NFPCs vary with fiber type, source, and structure. Several drawbacks of NFPCs, e.g., higher water absorption rate, inferior fire resistance, and lower mechanical properties, have limited their applications. This has necessitated the development of good practice in systematic engineering design in order to attain optimized NRPC products. Product design and manufacturing engineering need to move in a mutually considerate manner in order to produce successful natural fiber-based composite material products. The design process involves concept design, material selection, and finally, the manufacturing of the design. Numerous products have been commercialized using natural fibers, e.g., sports equipment, musical instruments, and electronic products. In the end, this review provides a guideline for the product design process based on natural fibers, which subsequently leads to a sustainable design.
Polymer composites filled with metal derivatives have been widely used in recent years, particularly as flame retardants, due to their superior characteristics, including high thermal behavior, low environmental degradation, and good fire resistance. The hybridization of metal and polymer composites produces various favorable properties, making them ideal materials for various advanced applications. The fire resistance performance of polymer composites can be enhanced by increasing the combustion capability of composite materials through the inclusion of metallic fireproof materials to protect the composites. The final properties of the metal-filled thermoplastic composites depend on several factors, including pore shape and distribution and morphology of metal particles. For example, fire safety equipment uses polyester thermoplastic and antimony sources with halogenated additives. The use of metals as additives in composites has captured the attention of researchers worldwide due to safety concern in consideration of people's life and public properties. This review establishes the state-of-art flame resistance properties of metals/polymer composites for numerous industrial applications.
Nowadays, pultruded glass fiber-reinforced polymer composite (PGFRPC) structures have been used widely for cross-arms in high transmission towers. These composite structures have replaced cross-arms of conventional materials like wood due to several factors, such as better strength, superior resistance to environmental degradation, reduced weight, and comparatively cheaper maintenance. However, lately, several performance failures have been found on existing cross-arm members, caused by moisture, temperature changes in the atmosphere, and other environmental factors, which may lead to a complete failure or reduced service life. As a potential solution for this problem, enhancing PGFRPC with honeycomb-filled composite structures will become a possible alternative that can sustain a longer service life compared to that of existing cross-arms. This is due to the new composite structures' superior performance under mechanical duress in providing better stiffness, excellence in flexural characteristics, good energy absorption, and increased load-carrying capacity. Although there has been a lack of previous research done on the enhancement of existing composite cross-arms in applications for high transmission towers, several studies on the enhancement of hollow beams and tubes have been done. This paper provides a state-of-the-art review study on the mechanical efficiency of both PGFRPC structures and honeycomb-filled composite sandwich structures in experimental and analytical terms.
A novel class of carbon nanotube (CNT)-based nanomaterials has been surging since 1991 due to their noticeable mechanical and electrical properties, as well as their good electron transport properties. This is evidence that the development of CNT-reinforced polymer composites could contribute in expanding many areas of use, from energy-related devices to structural components. As a promising material with a wide range of applications, their poor solubility in aqueous and organic solvents has hindered the utilizations of CNTs. The current state of research in CNTs-both single-wall carbon nanotubes (SWCNT) and multiwalled carbon nanotube (MWCNT)-reinforced polymer composites-was reviewed in the context of the presently employed covalent and non-covalent functionalization. As such, this overview intends to provide a critical assessment of a surging class of composite materials and unveil the successful development associated with CNT-incorporated polymer composites. The mechanisms related to the mechanical, thermal, and electrical performance of CNT-reinforced polymer composites is also discussed. It is vital to understand how the addition of CNTs in a polymer composite alters the microstructure at the micro- and nano-scale, as well as how these modifications influence overall structural behavior, not only in its as fabricated form but also its functionalization techniques. The technological superiority gained with CNT addition to polymer composites may be advantageous, but scientific values are here to be critically explored for reliable, sustainable, and structural reliability in different industrial needs.
The application of pultruded glass fiber-reinforced polymer composites (PGFRPCs) as a replacement for conventional wooden cross-arms in transmission towers is relatively new. Although numerous studies have conducted creep tests on coupon-scale PGFRPC cross-arms, none had performed creep analyses on full-scale PGFRPC cross-arms under actual working load conditions. Thus, this work proposed to study the influence of an additional bracing system on the creep responses of PGFRPC cross-arms in a 132 kV transmission tower. The creep behaviors and responses of the main members in current and braced PGFRPC cross-arm designs were compared and evaluated in a transmission tower under actual working conditions. These PGFRPC cross-arms were subjected to actual working loads mimicking the actual weight of electrical cables and insulators for a duration of 1000 h. The cross-arms were installed on a custom test rig in an open area to simulate the actual environment of tropical climate conditions. Further creep analysis was performed by using Findley and Burger models on the basis of experimental data to link instantaneous and extended (transient and viscoelastic) creep strains. The addition of braced arms to the structure reduced the total strain of a cross-arm's main member beams and improved elastic and viscous moduli. The addition of bracing arms improved the structural integrity and stiffness of the cross-arm structure. The findings of this study suggested that the use of a bracing system in cross-arm structures could prolong the structures' service life and subsequently reduce maintenance effort and cost for long-term applications in transmission towers.
The interest in using natural fiber reinforced composites is now at its highest. Numerous studies have been conducted due to their positive benefits related to environmental issues. Even though they have limitations for some load requirements, this drawback has been countered through fiber treatment and hybridization. Sandwich structure, on the other hand, is a combination of two or more individual components with different properties, which when joined together can result in better performance. Sandwich structures have been used in a wide range of industrial material applications. They are known to be lightweight and good at absorbing energy, providing superior strength and stiffness-to-weight ratios, and offering opportunities, through design integration, to remove some components from the core element. Today, many industries use composite sandwich structures in a range of components. Through good design of the core structure, one can maximize the strength properties, with a low density. However, the application of natural fiber composites in sandwich structures is still minimal. Therefore, this paper reviewed the possibility of using a natural fiber composite in sandwich structure applications. It addressed the mechanical properties and energy-absorbing characteristics of natural fiber-based sandwich structures tested under various compression loads. The results and potential areas of improvement to fit into a wide range of engineering applications were discussed.
As a result of their significant importance and applications in vast areas, including oil and gas, building construction, offshore structures, ships, and bridges, coating materials are regularly exposed to harsh environments which leads to coating delamination. Therefore, optimum interfacial bonding between coating and substrate, and the reason behind excellent adhesion strength is of utmost importance. However, the majority of studies on polymer coatings have used a one-factor-at-a-time (OFAT) approach. The main objective of this study was to implement statistical analysis in optimizing the factors to provide the optimum adhesion strength and to study the microstructure of a rice husk ash (RHA)-based geopolymer composite coating (GCC). Response surface methodology was used to design experiments and perform analyses. RHA/alkali activated (AA) ratio and curing temperature were chosen as factors. Adhesion tests were carried out using an Elcometer and a scanning electron microscope was used to observe the microstructure. Results showed that an optimum adhesion strength of 4.7 MPa could be achieved with the combination of RHA/AA ratio of 0.25 and curing temperature at 75 °C. The microstructure analysis revealed that coating with high adhesion strength had good interfacial bonding with the substrate. This coating had good wetting ability in which the coating penetrated the valleys of the profiles, thus wetting the entire substrate surface. A large portion of dense gel matrix also contributed to the high adhesion strength. Conversely, a large quantity of unreacted or partially reacted particles may result in low adhesion strength.
Nanofibrillated cellulose (NFCs) were extracted from sugar palm fibres (SPS) in two separate stages; delignification and mercerization to remove lignin and hemicellulose, respectively. Subsequently, the obtained cellulose fibres were then mechanically extracted into nanofibres using high pressurized homogenization (HPH). The diameter distribution sizes of the isolated nanofibres were dependent on the cycle number of HPH treatment. TEM micro-images displayed the decreasing trend of NFCs diameter, from 21.37 to 5.5 nm when the number of cycle HPH was increased from 5 to 15 cycles, meanwhile TGA and XRD analysis showed that the degradation temperature and crystallinity of the NFCs were slightly increased from 347 to 347.3 °C and 75.38 to 81.19% respectively, when the number of cycles increased. Others analysis also were carried on such as FT-IR, FESEM, AFM, physical properties, zeta potential and yield analysis. The isolated NFCs may be potentially applied in various application, such as tissue engineering scaffolds, bio-nanocomposites, filtration media, bio-packaging and etc.
Sugar palm fibre (SPF) was treated with NaClO2, bleached with NaOH and subsequently hydrolyzed with acid to obtain sugar palm nanocrystalline cellulose (SPNCCs). Bionanocomposites in the form of films were prepared by mixing sugar palm starch (SPS) and sorbitol/glycerol with different nanofiller SPNCCs compositions (0-1.0 wt%) using solution casting method. The resulting fibres and nanocomposites were characterized in terms of morphology (FESEM and TEM), footprint, crystallinity (XRD), light transmittance, biodegradability, physical, water barrier, thermal (TGA, DSC and DMA) and mechanical properties. The length (L), diameter (D) and L/D values of the SPNCCs were 130 ± 30.23, 8.5 ± 1.82 nm, and 15.3, respectively. The SPS/SPNCCs nanocomposite films exhibited higher crystallinity, tensile strength, Young's modulus, thermal and water-resistance compared to the neat SPS film. The results showed that the tensile strength and moduli of the bionanocomposites increased after being reinforced with SPNCCs and the optimum nanofiller content was 0.5%.
Steel sections are normally shaped via cold work manufacturing processes. The extent of cold work to shape the steel sections might induce residual stresses in the region of bending. Previously, researchers had performed studies on the influences of local buckling on the failure behavior of steel compression members which shown that failure will happen when most of the yielding has extended to the middle surface in the bend region of the sections. Therefore, these cold work methods may have major effect on the behavior of the steel section and also its load-bearing capability. In addition, another factor may play significant role in formed section's load-bearing capacity which is the longitudinal residual strain. The longitudinal residual strain raised during forming procedure can be used to define the section imperfection of the formed section and its relation to the existence of defects. Therefore, the main motivation of this research paper is to perform three-dimensional finite element (3D-FE) to investigate peak longitudinal residual strains of a thin-walled steel plate with large bending angle along member length. A 3D finite element simulation in ABAQUS has been employed to simulate this forming process. The study concluded that the longitudinal residual strain at the section corner edge was higher than those at the rest of the corner region. These strains at the edge were higher than the yield strain
(
ε
y
)
of the formed section which occurred due to the lack of transverse restraint. This made the plate edge tended to bend toward the normal direction when it was under a high transverse bending. This causes a significant difference in longitudinal strain at the plate edge.
Cellulose was extracted from sugar palm fibres (Arenga pinnata) by conducting delignification and mercerization treatments. Subsequently, sugar palm nanocrystalline celluloses (SPNCCs) were isolated from the extracted cellulose with 60wt% concentrated sulphuric acid. The chemical composition of sugar palm fibres were determined at different stages of treatment. Structural analysis was carried out by Brunauer-Emmett-Teller (BET), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR). Morphological analysis of extracted cellulose and isolated nanocrystalline cellulose (NCCs) was investigated by using field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM), and transmission electron microscopy (TEM). The thermal stability of sugar palm fibres at different stages of treatment was investigated by thermogravimetric analysis (TGA). The results showed that lignin and hemicellulose were removed from the extracted cellulose through the delignification and mercerization process, respectively. The isolated SPNCCs were found to have length and diameters of 130±30nm and 9±1.96nm, respectively.
The aim of this paper is to investigate the characteristics of thermoplastic sugar palm starch/agar (TPSA) blend containing Eucheuma cottonii seaweed waste as biofiller. The composites were prepared by melt-mixing and hot pressing at 140°C for 10min. The TPSA/seaweed composites were characterized for their mechanical, thermal and biodegradation properties. Incorporation of seaweed from 0 to 40wt.% has significantly improved the tensile, flexural, and impact properties of the TPSA/seaweed composites. Scanning electron micrograph of the tensile fracture showed homogeneous surface with formation of cleavage plane. It is also evident from TGA results that thermal stability of the composites were enhanced with addition of seaweed. After soil burial for 2 and 4 weeks, the biodegradation of the composites was enhanced with addition of seaweed. Overall, the incorporation of seaweed into TPSA enhances the properties of TPSA for short-life product application such as tray, plate, etc.