Metal-based adsorbents with varying active phase loadings were synthesized to capture hydrogen sulfide (H2S) from a biogas mimic system. The adsorption-desorption cycles were implemented to ascertain the H2S captured. All prepared adsorbents were evaluated by nitrogen adsorption, Brunauer-Emmett-Teller surface area analysis, scanning electron microscopy-energy-dispersive X-ray spectroscopy, and Fourier transform infrared spectroscopy. From the results, modified adsorbents, dual chemical mixture (DCM) and a core-shell (CS) had the highest H2S adsorption performance with a range of 0.92-1.80 mg H2S/g. After several cycles of heat/N2 regeneration, the total H2S adsorption capacity of the DCM adsorbent decreased by 62.1%, whereas the CS adsorbent decreased by only 25%. Meanwhile, the proposed behavioral model for H2S adsorption-desorption was validated effectively using various analyses throughout the three cycles of adsorption-desorption samples. Moreover, as in this case, the ZnAc2/ZnO/CAC_OS adsorbents show outstanding performances with 30 cycles of adsorption-desorption compared to only 12 cycles of ZnAc2/ZnO/CAC_DCM. Thus, this research paper will provide fresh insights into adsorption-desorption behavior through the best adsorbents' development and the adsorbents' capability at the highest number of adsorption-desorption cycles.
This study reports on the synthesis of bi-metal compound (BMC) adsorbents based on commercial coconut activated carbon (CAC), surface-modified with metal acetate (ZnAc2), metal oxide (ZnO), and the basic compounds potassium hydroxide (KOH) and sodium hydroxide (NaOH). The adsorbents were then characterized by scanning electron microscopy and elemental analysis, microporosity analysis through Brunauer-Emmett-Teller (BET) analysis, and thermal stability via thermogravimetric analysis. Adsorption-desorption test was conducted to determine the adsorption capacity of H2S via 1 L adsorber and 1000 ppm H2S balanced 49.95% for N2 and CO2. Characterization results revealed that the impregnated solution homogeneously covered the adsorbent surface, morphology, and properties. The adsorption test result reveals that the ZnAc2/ZnO/CAC_B had a higher H2S breakthrough adsorption capacity and performed at larger than 90% capability compared with a single modified adsorbent (ZnAc2/CAC). Therefore, the synthesized BMC adsorbents have a high H2S loading, and the abundance and low cost of CAC may lead to favorable adsorbents in H2S captured.
In this work, the performance of anion exchange membrane (AEM) electrolysis is evaluated. A parametric study is conducted, focusing on the effects of various operating parameters on the AEM efficiency. The following parameters-potassium hydroxide (KOH electrolyte concentration (0.5-2.0 M), electrolyte flow rate (1-9 mL/min), and operating temperature (30-60 °C)-were varied to understand their relationship to AEM performance. The performance of the electrolysis unit is measured by its hydrogen production and energy efficiency using the AEM electrolysis unit. Based on the findings, the operating parameters greatly influence the performance of AEM electrolysis. The highest hydrogen production was achieved with the operational parameters of 2.0 M electrolyte concentration, 60 °C operating temperature, and 9 mL/min electrolyte flow at 2.38 V applied voltage. Hydrogen production of 61.13 mL/min was achieved with an energy consumption of 48.25 kW·h/kg and an energy efficiency of 69.64%.
An investigation was conducted to determine the effects of operating parameters for various electrode types on hydrogen gas production through electrolysis, as well as to evaluate the efficiency of the polymer electrolyte membrane (PEM) electrolyzer. Deionized (DI) water was fed to a single-cell PEM electrolyzer with an active area of 36 cm2. Parameters such as power supply (50-500 mA/cm2), feed water flow rate (0.5-5 mL/min), water temperature (25-80 °C), and type of anode electrocatalyst (0.5 mg/cm2 PtC [60%], 1.5 mg/cm2 IrRuOx with 1.5 mg/cm2 PtB, 3.0 mg/cm2 IrRuOx, and 3.0 mg/cm2 PtB) were varied. The effects of these parameter changes were then analyzed in terms of the polarization curve, hydrogen flowrate, power consumption, voltaic efficiency, and energy efficiency. The best electrolysis performance was observed at a DI water feed flowrate of 2 mL/min and a cell temperature of 70 °C, using a membrane electrode assembly that has a 3.0 mg/cm2 IrRuOx catalyst at the anode side. This improved performance of the PEM electrolyzer is due to the reduction in activation as well as ohmic losses. Furthermore, the energy consumption was optimal when the current density was about 200 mA/cm2, with voltaic and energy efficiencies of 85% and 67.5%, respectively. This result indicates low electrical energy consumption, which can lower the operating cost and increase the performance of PEM electrolyzers. Therefore, the optimal operating parameters are crucial to ensure the ideal performance and durability of the PEM electrolyzer as well as lower its operating costs.