Demand for diesel continues to increase due to rapid population growth, which could contribute to fossil fuel exhaustion. Biodiesel has been widely developed as a replacement for conventional diesel to resolve the issue. Biodiesel production from waste cooking oil (WCO) was carried out via the transesterification process using two types of bentonite catalysts, which are raw bentonite and NaOH/bentonite. By using the impregnation method, the NaOH/bentonite catalyst was synthesized at 60°C for 12 hours. The transesterification was conducted with 0.5wt% of catalyst, at 15:1 (methanol- to-oil), for 2 hours at different reaction temperatures. The characterization of both raw bentonite and NaOH/bentonite was done using X-ray Diffraction (XRD) and Brunauer, Emmett, Teller (BET) surface characterization. A high yield of FAMEs (72%) was found to be obtained in continuous stirring at 55ºC for 2 hours and 15:1 methanol/oil molar ratio with 0.5wt.% (0.15g) of NaOH/bentonite catalyst.
This paper reports a study of the formation of cellulose nanofibres from kenaf waste using chemical
extraction method. The extracted holocellulose was then prepared for acid hydrolysis to form the
cellulose. Before mixing it with polyvinyl chloride (PVA) solution and extruded using electrospinning
under different parameters to produce PVA/kenaf nanofibres. Results showed that the morphological
structures of PVA/kenaf nanofibres varied at different voltages. An increase in voltage from 10 kV to 20
kV produced more beads along the fibre length. In addition, the applied voltages were found to affect the
resultant fibre diameter of the PVA/kenaf nanofibres. The results also showed that the electrospinning
parameters affect the shapes of the PVA/kenaf nanofibre membranes. Based on the experimental works,
the optimal applied voltage was found to be at 15 kV, where the resultant fibre diameter and membrane
coverage area were approximately 43.9 ± 3.1 nm and 214.2 ± 15.8 cm2
, respectively.
Oil palm (Elaeis guineensis Jacq.) is one of the most important commercial crops for the production of palm oil, which generates 10.88 tons of oil palm fronds per hectare of plantation as a by-product. In this study, oil palm frond fibres were subjected to an autohydrolysis treatment using an autoclave, operated at 121 °C for 20-80 min, to facilitate the separation of hemicelluloses. The hemicellulose-rich solution (autohydrolysate) was subjected to further hydrolysis with 4-16 U of mixed Trichoderma viride endo-(1,4)-β-xylanases (EC 3.2.1.8) per 100 mg of autohydrolysate. Autoclaving of palm fronds at 121°C for 60 min (a severity factor of 2.40) recovered 75% of the solid residue, containing 57.9% cellulose and 18% Klason lignin, and an autohydrolysate containing 14.94% hemicellulose, with a fractionation efficiency of 49.20%. Subsequent enzymatic hydrolysis of the autohydrolysate with 8 U of endoxylanase at 40 °C for 24 h produced a solution containing 17.5% xylooligosaccharides and 25.6% xylose. The results clearly indicate the potential utilization of oil palm frond, an abundantly available lignocellulosic biomass for the production of xylose and xylooligosaccharides which can serve as functional food ingredients.
Steam explosion of oil palm frond has been carried out under different temperatures between 180 and 210°C for 4 min (severity of 2.96-3.84) after impregnation of the frond chips with water or KOH solution. The effects of impregnation and steam explosion conditions of oil palm fronds on the water soluble fraction and insoluble fraction were investigated. The maximum yield of hemicelluloses in water soluble fractions recovered was 23.49% and 25.33% for water and KOH impregnation, treated with steam explosion at temperature of 210°C (severity of 3.84) with a fractionation efficiency of 77.30% and 83.32%, respectively. Under this condition, the water insoluble fractions contained celluloses at 60.83% and 64.80% for water and KOH impregnation, respectively. The steam explosion temperature of 210°C for 4 min (logR(o) 3.84) was found to be the best condition in the extraction of hemicelluloses from OPF for both types of impregnation.